表面沉积氯化钠的7A04铝合金在模拟环境中的腐蚀行为

来源期刊:中国有色金属学报2009年第5期

论文作者:周和荣 马坚 李晓刚 陆启凯 冯皓 揭敢新

文章页码:974 - 980

关键词:7A04铝合金;大气腐蚀;模拟环境

Key words:7A04 aluminum alloy; atmospheric corrosion; simulated environment

摘    要:在实验室模拟条件下((25±2) ℃,相对湿度(95±5)%),采用增重法、扫描电子显微镜、傅立叶红外光谱和X射线衍射等方法研究氯化钠和几种模拟环境气氛对7A04铝合金大气腐蚀行为的影响,并对其腐蚀机理进行讨论。结果表明:表面沉积氯化钠的7A04铝合金在几种模拟气氛环境中均明显地加速了材料的腐蚀;随腐蚀时间的延长,腐蚀产物不断增多;腐蚀产物微观形貌呈团块状且凹凸不平;腐蚀增重Δm/A与暴露时间t之间符合指数衰减规律;气氛腐蚀性由强到弱的顺序为50×10-6 SO2>1%CO2>空气。

Abstract: The corrosion behavior of 7A04 aluminum alloy deposited with NaCl in several simulated environments ((25±2) ℃ and relative humidity (RH) (95±5)%) was investigated by mass gain method, Fourier transform infrared spectroscope, scanning electron microscopy and X-ray diffractometry. The corrosion mechanism for aluminum alloy was discussed. The results show that NaCl can evidently accelerate the atmospheric corrosion of 7A04 aluminum alloy in several simulated environments. The corrosion products increase with prolonging corrosion time. The surface observation reveals that the corrosion products are agglomerate and accidented. The relationship between mass gain of corrosion product and time accords with the exponential attenuation rule. The corrosion sequence of corrosion mediums from strong to ebb is 50×10-6 SO2>1%CO2>air.

基金信息:国家自然科学基金资助项目
科技部科技基础条件平台建设资助项目

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号