Microstructure and Properties of 3.5 vol.%TiBw/Ti6A14V Composite Tubes Fabricated by Hot-hydrostatic Extrusion

来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2014年第7期

论文作者:Wencong Zhang Xueyan Jiao Yang Yu Jianlei Yang Yangju Feng

文章页码:710 - 714

摘    要:Tubes of 3.5 vol.%TiB whiskers reinforced Ti6AI4 V matrix composites(TiBw/Ti6AI4V) were successfully fabricated by a two-step hot-hydrostatic extrusion process:β extrusion at 1100 ℃ and subsequent near-βextrusion at 950 ℃.The dimensions of tubes were about 7 mm in diameter and 2 mm in thickness.A refined basket-weave structure in Ti6AI4 V matrix was achieved at ambient temperature after the extrusion process.Besides,the original network structure formed by TiB whiskers synthesized was broken,while the TiB whiskers were preferentially aligned in the extruding direction.Meanwhile,a fibrous texture was evolved finally,resulting from partial dynamic recrystallization during the β extrusion and the involvement of a phase during the near-β extrusion.The tensile and compressive tests results showed that both the strength and ductility of the tubes were significantly improved.In particular,the tubes exhibited good mechanical properties at elevated temperatures.

详情信息展示

Microstructure and Properties of 3.5 vol.%TiBw/Ti6A14V Composite Tubes Fabricated by Hot-hydrostatic Extrusion

Wencong Zhang,Xueyan Jiao,Yang Yu,Jianlei Yang,Yangju Feng

School of Materials Science and Engineering,Harbin Institute of Technology at Weihai

摘 要:Tubes of 3.5 vol.%TiB whiskers reinforced Ti6AI4 V matrix composites(TiBw/Ti6AI4V) were successfully fabricated by a two-step hot-hydrostatic extrusion process:β extrusion at 1100 ℃ and subsequent near-βextrusion at 950 ℃.The dimensions of tubes were about 7 mm in diameter and 2 mm in thickness.A refined basket-weave structure in Ti6AI4 V matrix was achieved at ambient temperature after the extrusion process.Besides,the original network structure formed by TiB whiskers synthesized was broken,while the TiB whiskers were preferentially aligned in the extruding direction.Meanwhile,a fibrous texture was evolved finally,resulting from partial dynamic recrystallization during the β extrusion and the involvement of a phase during the near-β extrusion.The tensile and compressive tests results showed that both the strength and ductility of the tubes were significantly improved.In particular,the tubes exhibited good mechanical properties at elevated temperatures.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号