Effect of rare earths on microwave absorbing properties of RE-Co alloys
来源期刊：Journal of Rare Earths2015年第3期
论文作者：何崇康 潘顺康 成丽春 刘星 吴亚军
文章页码：271 - 276
摘 要：The powders of RE2Co17（RE=Y, Ce, Nd, Ho, Er） and Ho x Co100–x（x=6, 8, 10, 12） alloys were prepared by the arc melting method and high-energy ball mill process. The compositions and morphologies of the alloys were characterized by X-ray diffraction（XRD） and scanning electron microscopy（SEM）, and the microwave absorbing properties were studied by a vector network analyzer. The results showed that the alloy of Y2Co17 had better absorbing properties at low frequencies and its lowest reflectivity value was –9.5 d B at 3.8 GHz. The lowest reflectivity value of Ho2Co17 alloy was –13.7 d B at 7.02 GHz and it obtained large absorbing bandwidth. Reflectivity value less than –5 d B was from 5.1 to 10.2 GHz. When x=6 and x=8, the alloys of Ho x Co100–x consisted of Ho2Co17 phase and Co phase. They had good radar absorbing properties. With increase in Ho content, the minimum reflectivity value worsened and the absorbing peak frequency shifted toward higher frequencies. But when x=12, the absorbing peak frequency shifted toward lower frequencies but the minimum reflectivity value worsened.
何崇康1,2，潘顺康1，成丽春1,3，刘星1，吴亚军1
1. School of Materials Science and Engineering, Guilin University of Electronic Technology2. Hezhou Science and Technology Bureau3. School of Materials Science and Engineering, Central South University
摘 要：The powders of RE2Co17（RE=Y, Ce, Nd, Ho, Er） and Ho x Co100–x（x=6, 8, 10, 12） alloys were prepared by the arc melting method and high-energy ball mill process. The compositions and morphologies of the alloys were characterized by X-ray diffraction（XRD） and scanning electron microscopy（SEM）, and the microwave absorbing properties were studied by a vector network analyzer. The results showed that the alloy of Y2Co17 had better absorbing properties at low frequencies and its lowest reflectivity value was –9.5 d B at 3.8 GHz. The lowest reflectivity value of Ho2Co17 alloy was –13.7 d B at 7.02 GHz and it obtained large absorbing bandwidth. Reflectivity value less than –5 d B was from 5.1 to 10.2 GHz. When x=6 and x=8, the alloys of Ho x Co100–x consisted of Ho2Co17 phase and Co phase. They had good radar absorbing properties. With increase in Ho content, the minimum reflectivity value worsened and the absorbing peak frequency shifted toward higher frequencies. But when x=12, the absorbing peak frequency shifted toward lower frequencies but the minimum reflectivity value worsened.
关键词：