Microstructure and mechanical properties of as-cast Mg-5Sn-2Ce-xZn alloys

来源期刊:JOURNAL OF RARE EARTHS2017年第6期

论文作者:丁武成 陈云贵 肖素芬 崔志明 程鹏

文章页码:585 - 592

摘    要:The microstructure, mechanical properties and compression creep resistance of as-cast Mg-5Sn-2Ce-xZn(x=0, 2 wt.%, 4 wt.%) alloys were investigated in this paper. The results showed that the Ce-containing compounds were MgS nC e phase and an unknown phase, and they were the dominant intermetallics in as-cast Mg-5Sn-2Ce-xZn alloys. At x=0 wt.%, the Ce-containing compounds formed in interdendritic regions with the shape of rod. As the Zn content was increased to 2 wt.%, the Ce-containing compounds partly changed from rod-like to sheet-like. However, there were few further changes in the Ce-containing compounds with further increase in Zn content to 4 wt.%. Compared with Mg-5Sn-2Ce alloy, the tensile strength and elongation of the alloy containing 4 wt.% Zn increased by 39% and 112%, respectively, and the secondary creep rate(175 °C/55 MPa) decreased at least by an order of magnitude. These improvement could be attributed to the combined effects of the high content of Zn dissolving in a-Mg matrix and the modification of Ce-containing compounds by Zn addition.

详情信息展示

Microstructure and mechanical properties of as-cast Mg-5Sn-2Ce-xZn alloys

丁武成,陈云贵,肖素芬,崔志明,程鹏

College of Materials Science and Engineering, Sichuan University

摘 要:The microstructure, mechanical properties and compression creep resistance of as-cast Mg-5Sn-2Ce-xZn(x=0, 2 wt.%, 4 wt.%) alloys were investigated in this paper. The results showed that the Ce-containing compounds were MgS nC e phase and an unknown phase, and they were the dominant intermetallics in as-cast Mg-5Sn-2Ce-xZn alloys. At x=0 wt.%, the Ce-containing compounds formed in interdendritic regions with the shape of rod. As the Zn content was increased to 2 wt.%, the Ce-containing compounds partly changed from rod-like to sheet-like. However, there were few further changes in the Ce-containing compounds with further increase in Zn content to 4 wt.%. Compared with Mg-5Sn-2Ce alloy, the tensile strength and elongation of the alloy containing 4 wt.% Zn increased by 39% and 112%, respectively, and the secondary creep rate(175 °C/55 MPa) decreased at least by an order of magnitude. These improvement could be attributed to the combined effects of the high content of Zn dissolving in a-Mg matrix and the modification of Ce-containing compounds by Zn addition.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号