Electronic Transport Properties of La2/3Ca1/3Mn0.98Cu0.02O3 Sintered at Different Temperature
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2009年第2期
论文作者:胡清华
文章页码:300 - 303
摘 要:The sol-gel method was adopted to prepare series of La2/3Ca1/3Mn0.98Cu0.02O3 samples sintered at different temperatures, and the structure of samples, high-temperature electrical conductive mechanism and electronic transport properties of double-peak resistance were investigated. X-ray diffraction pattern indicates that the samples are in perovskite structures and obey the Variable-Rang Hopping Mechanism of ρ=ρ0exp[(T0/T)1/4] under high temperatures during the electrical conduction. In addition, based on the polycrystalline granular system surface and image, the reasonable explanation was given for the double-peak resistance phemomenon.
胡清华
School of Science, Wuhan University of Technology
摘 要:The sol-gel method was adopted to prepare series of La2/3Ca1/3Mn0.98Cu0.02O3 samples sintered at different temperatures, and the structure of samples, high-temperature electrical conductive mechanism and electronic transport properties of double-peak resistance were investigated. X-ray diffraction pattern indicates that the samples are in perovskite structures and obey the Variable-Rang Hopping Mechanism of ρ=ρ0exp[(T0/T)1/4] under high temperatures during the electrical conduction. In addition, based on the polycrystalline granular system surface and image, the reasonable explanation was given for the double-peak resistance phemomenon.
关键词: