Optical and acoustic phonon modes confined in gallium phosphide nanoparticles

来源期刊:Rare Metals2010年第6期

论文作者:ZHANG Zhaochun and ZHANG Neng School of Material Science and Engineering,Shanghai University,Shanghai ,China

文章页码:561 - 566

摘    要:The main aim of this paper is to discuss the confinement effects on the optical and acoustic phonon vibrational modes in gallium phosphide(GaP) nanoparticles(cylindric grain).The Raman scattering from the GaP nanoparticles was investigated.It was found that the red-shifts of the longitudinal optical(LO) mode and transverse optical(TO) mode were 15 cm?1 and 13.8 cm?1,respectively.It is generally accepted that the red-shifts of the optical phonon modes are due to the presence of smaller nanosized particles(~1.2 nm) acting as the nanoclustered building blocks of the GaP nanoparticles.In the low frequency Raman spectrum,a set of Stokes lines with almost the same spacing was clearly observed.The scattering feature originates from the discrete phonon density of states of the nanoclustered building blocks.According to Lamb’s vibrational theory,the Raman shift wavenumbers of the spheroidal mode and torsional mode of the lowest energy surface modes for the nanoclustered building blocks were calculated.Good agreement can be achieved between the calculated results and the observed scattering peaks.These results indicate that the corresponding Raman peaks are due to scattering from the localized acoustic phonons in the nanoclustered building blocks in the GaP nanoparticles.

详情信息展示

Optical and acoustic phonon modes confined in gallium phosphide nanoparticles

摘要:The main aim of this paper is to discuss the confinement effects on the optical and acoustic phonon vibrational modes in gallium phosphide(GaP) nanoparticles(cylindric grain).The Raman scattering from the GaP nanoparticles was investigated.It was found that the red-shifts of the longitudinal optical(LO) mode and transverse optical(TO) mode were 15 cm?1 and 13.8 cm?1,respectively.It is generally accepted that the red-shifts of the optical phonon modes are due to the presence of smaller nanosized particles(~1.2 nm) acting as the nanoclustered building blocks of the GaP nanoparticles.In the low frequency Raman spectrum,a set of Stokes lines with almost the same spacing was clearly observed.The scattering feature originates from the discrete phonon density of states of the nanoclustered building blocks.According to Lamb’s vibrational theory,the Raman shift wavenumbers of the spheroidal mode and torsional mode of the lowest energy surface modes for the nanoclustered building blocks were calculated.Good agreement can be achieved between the calculated results and the observed scattering peaks.These results indicate that the corresponding Raman peaks are due to scattering from the localized acoustic phonons in the nanoclustered building blocks in the GaP nanoparticles.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号