粘土固化浆液无侧限抗压强度增长规律及其影响因素

来源期刊:中国有色金属学报1999年第1期

论文作者:王星华 李炜

文章页码:180 - 184

关键词:粘土固化浆液,无侧限抗压强度,塑性强度

Key words:clay-hardening grouts (CHG), unconfined compressive strength, plastic strength

摘    要:研究了粘土固化浆液结石体无侧限抗压强度qu的增长规律及其影响因素, 得出以下结论: 粘土固化浆液无侧限抗压强度随时间的增加而增长, 其初期强度增长较快, 后期强度增长较慢; 增加水泥的加量将提高浆液的qu值, 固化剂A的加量有一最佳值(3%左右); 因固化剂B是作为加快水泥水化反应速度的催化剂而加入的, 所以, 固化剂B的加量以控制在5%以下为好。 此外, 还简单分析了粘土固化浆液结石体无侧限抗压强度与塑性强度存在差异的原因。

Abstract: The strength of grouts is a very important performance parameter during grouting. The affecting factors and growing rule of unconfined compressive strength of clay-hardening Grouts (CHG) were studied. The results showed that the unconfined compressive strength of CHG increases with the increasing of time; the early strength increases quickly, and the late strength increases slowly; increasing cement amount will increase the strength of CHG; the best amount of solidified agent (SA) A is 3%, the amount of SA B should be controlled under 5% because SA B is added into CHG as a catalyst increasing action rate of cement hydration. And then the reason that causes the difference between unconfined compressive strength and plastic strength of CHG was simply analyzed.

详情信息展示

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号