Carbonation Resistance of Sulphoaluminate Cement-based High Performance Concrete
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2009年第4期
论文作者：张德成
文章页码：663 - 666
摘 要：The influences of water/cement ratio and admixtures on carbonation resistance of sulphoaluminate cement-based high performance concrete （HPC） were investigated. The experimental results show that with the decreasing water/cement ratio, the carbonation depth of sulphoaluminate cement-based HPC is decreased remarkably, and the carbonation resistance capability is also improved with the adding admixtures. The morphologies and structure characteristics of sulphoaluminate cement hydration products before and after carbonation were analyzed using SEM and XRD. The analysis results reveal that the main hydration product of sulphoaluminate cement, that is ettringite （AFt）, decomposes after carbonation.
张德成
School of Materials Science and Engineering ,Wuhan University of TechnologySchool of Materials Science and Engineering,University of Jinan
摘 要：The influences of water/cement ratio and admixtures on carbonation resistance of sulphoaluminate cement-based high performance concrete （HPC） were investigated. The experimental results show that with the decreasing water/cement ratio, the carbonation depth of sulphoaluminate cement-based HPC is decreased remarkably, and the carbonation resistance capability is also improved with the adding admixtures. The morphologies and structure characteristics of sulphoaluminate cement hydration products before and after carbonation were analyzed using SEM and XRD. The analysis results reveal that the main hydration product of sulphoaluminate cement, that is ettringite （AFt）, decomposes after carbonation.
关键词：