Sigma Phase Precipitation and Properties of Super-duplex Stainless Steel UNS S32750 Aged at the Nose Temperature
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第2期
论文作者：邹德宁
文章页码：183 - 186
摘 要：The nose temperature for σ-phase precipitation in super-duplex stainless steel （SDSS） UNS S32750 was evaluated by hardness method.Color-optical microscopy,scanning electron microscopy,energy spectrum analysis,impact and corrosion testing were carried out to investigate characteristics of microstructure and properties of the SDSS aged at the nose temperature.The experimental results indicate that the nose temperature of precipitation is 920℃ and aging at this temperature tiny σ phases can precipitate at phase interfaces or ferrite grain boundaries within 2min.Prolonging aging duration the amount ofσ-phase increases and a dual structure with σ and γ is obtained when aging for 120min.The precipitation ofσ-phase leads to severe deterioration in impact toughness （longitudinal/transverse direction） and corrosion resistance of SDSS.
邹德宁
School of Metallurgy and Engineering,Xi’an University of Architecture and Technology
摘 要：The nose temperature for σ-phase precipitation in super-duplex stainless steel （SDSS） UNS S32750 was evaluated by hardness method.Color-optical microscopy,scanning electron microscopy,energy spectrum analysis,impact and corrosion testing were carried out to investigate characteristics of microstructure and properties of the SDSS aged at the nose temperature.The experimental results indicate that the nose temperature of precipitation is 920℃ and aging at this temperature tiny σ phases can precipitate at phase interfaces or ferrite grain boundaries within 2min.Prolonging aging duration the amount ofσ-phase increases and a dual structure with σ and γ is obtained when aging for 120min.The precipitation ofσ-phase leads to severe deterioration in impact toughness （longitudinal/transverse direction） and corrosion resistance of SDSS.
关键词：