Templating Synthesis and Luminescent Properties of SrAl2O4∶Eu, Dy Phosphor Derived from A Mesoporous Precursor
来源期刊：Journal of Rare Earths2007年第S1期
论文作者：杨雪峰 宁桂玲 潘文 潘文 林源
文章页码：321 - 325
摘 要：Long-lasting SrAl2O4∶Eu, Dy phosphor was successfully prepared from a mesoporous precursor. The precursor was synthesized by templating method using nonionic Polyethylene Oxide （PEO） as surfactants, which was proved by TG-DTG, X-Ray Diffraction （XRD） and Transmission Electron Microscopy （TEM） analysis. The analysis results indicated that regular cylindrical-to-hexagonal shaped pores with several nanometers were obtained. The structure and morphology of the SrAl2O4∶Eu, Dy phosphor by templating method was characterized by XRD and Scanning Electron Microscopy （SEM）. The XRD results showed that a pure SrAl2O4 phase formed at 900 ℃ by templating method. The SEM morphologies of the obtained phosphors prepared by templating synthesis were uniform and porous multicrystalline with average diameter size of 5 μm. The broad-band UV-excited SrAl2O4∶Eu, Dy phosphor derived from a mosoporous precursor was observed at λmax=515 nm due to the transitions from the 4f65d1 to the 4f7 configurations of Eu2+ ion. The main excitation and emission intensity of the phosphor with this method were stronger than that obtained by solid state reaction method. And the obtained long-lasting phosphor with this method revealed a better afterglow compared to the phosphor prepared through solid state reaction method.
杨雪峰，宁桂玲，潘文，刘红宇，林源
摘 要：Long-lasting SrAl2O4∶Eu, Dy phosphor was successfully prepared from a mesoporous precursor. The precursor was synthesized by templating method using nonionic Polyethylene Oxide （PEO） as surfactants, which was proved by TG-DTG, X-Ray Diffraction （XRD） and Transmission Electron Microscopy （TEM） analysis. The analysis results indicated that regular cylindrical-to-hexagonal shaped pores with several nanometers were obtained. The structure and morphology of the SrAl2O4∶Eu, Dy phosphor by templating method was characterized by XRD and Scanning Electron Microscopy （SEM）. The XRD results showed that a pure SrAl2O4 phase formed at 900 ℃ by templating method. The SEM morphologies of the obtained phosphors prepared by templating synthesis were uniform and porous multicrystalline with average diameter size of 5 μm. The broad-band UV-excited SrAl2O4∶Eu, Dy phosphor derived from a mosoporous precursor was observed at λmax=515 nm due to the transitions from the 4f65d1 to the 4f7 configurations of Eu2+ ion. The main excitation and emission intensity of the phosphor with this method were stronger than that obtained by solid state reaction method. And the obtained long-lasting phosphor with this method revealed a better afterglow compared to the phosphor prepared through solid state reaction method.
关键词：