Recrystallizaiton Behavior of Directionally Solidified DZ4 Superalloy
来源期刊：材料热处理学报2004年第5期
论文作者：TAO Chun-Hu LI Yun-ju ZHANG Wei-fang
关键词：directionally solidified superalloy; recrystallization; heat treatment; deformation;
摘 要：This article investigated effects of degrees of deformation, heat treatment temperatures and holding times on the recrystallization behavior of directionally solidified DZ4 superalloy. The results showed that, recrystallization of DZ4 superalloy could take place during solution heat treatment after certain degrees of cold work and depths of recrystallization increased with increasing degrees of deformation and heat treatment temperature. At the temperature below γ' solvus,prolonged holding times did not play an important role in improving recrystallization depths. Moreover, prevention measures for recrystallization of directionally solidified blades were given.
TAO Chun-Hu1，LI Yun-ju1，ZHANG Wei-fang1
(1.Failure Analysis Center of AVIC, Beijing Institute of Aeronautical Materials, Beijing, China)
摘要:This article investigated effects of degrees of deformation, heat treatment temperatures and holding times on the recrystallization behavior of directionally solidified DZ4 superalloy. The results showed that, recrystallization of DZ4 superalloy could take place during solution heat treatment after certain degrees of cold work and depths of recrystallization increased with increasing degrees of deformation and heat treatment temperature. At the temperature below γ'' solvus,prolonged holding times did not play an important role in improving recrystallization depths. Moreover, prevention measures for recrystallization of directionally solidified blades were given.
关键词:directionally solidified superalloy; recrystallization; heat treatment; deformation;
【全文内容正在添加中】