Application of X-ray Computed Tomography in Characterization Microstructure Changes of Cement Pastes in Carbonation Process
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2012年第2期
论文作者：韩建德 孙伟
文章页码：358 - 363
摘 要：The microstructure characteristics and meso-defect volume changes of hardened cement paste before and after carbonation were investigated by three-dimensional（3D）X-ray computed tomography（XCT）,where three types water-to-cement ratio of 0.53,0.35 and 0.23 were considered.The high-resolution 3D images of microstructure and filtered defects were reconstructed by an XCT VG Studio MAX 2.0 software.The meso-defect volume fractions and size distribution were analyzed based on 3D images through add-on modules of 3D defect analysis.The 3D meso-defects volume fractions before carbonation were 0.79%,0.38% and 0.05% corresponding to w/c ratio=0.53,0.35 and 0.23,respectively.The 3D meso-defects volume fractions after carbonation were 2.44%,0.91% and 0.14% corresponding to w/c ratio=0.53,0.35 and 0.23,respectively.The experimental results suggest that 3D meso-defects volume fractions after carbonation for above three w/c ratio increased significantly.At the same time,meso-cracks distribution of the carbonation shrinkage and gray values changes of the different w/c ratio and carbonation reactions were also investigated.
韩建德1,2，孙伟1,2
1. School of Materials Science and Engineering,Southeast University
摘 要：The microstructure characteristics and meso-defect volume changes of hardened cement paste before and after carbonation were investigated by three-dimensional（3D）X-ray computed tomography（XCT）,where three types water-to-cement ratio of 0.53,0.35 and 0.23 were considered.The high-resolution 3D images of microstructure and filtered defects were reconstructed by an XCT VG Studio MAX 2.0 software.The meso-defect volume fractions and size distribution were analyzed based on 3D images through add-on modules of 3D defect analysis.The 3D meso-defects volume fractions before carbonation were 0.79%,0.38% and 0.05% corresponding to w/c ratio=0.53,0.35 and 0.23,respectively.The 3D meso-defects volume fractions after carbonation were 2.44%,0.91% and 0.14% corresponding to w/c ratio=0.53,0.35 and 0.23,respectively.The experimental results suggest that 3D meso-defects volume fractions after carbonation for above three w/c ratio increased significantly.At the same time,meso-cracks distribution of the carbonation shrinkage and gray values changes of the different w/c ratio and carbonation reactions were also investigated.
关键词：