Electrodeposition and Characterization of CuInSe2 Thin Films for Solar Cells
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2007年第1期
论文作者：李建庄 赵修建
文章页码：140 - 143
摘 要：CuInSe2 （CIS） thin films were prepared by electrodeposition from the de-ionized water solution consisting of CuCl2, InCl3, H2SeO3 and Na-citrate onto Mo/soda-lime glass （SLG） substrates. A thermal processing in Se atmosphere at 450 ℃ was carried out for the electrodepositied films to improve the stoichiometry. The composition and morphology of selenized CIS thin films were studied using energy dispersive spectroscopy （EDS） and scanning electron microscopy （SEM）, respectively. X-ray diffraction （XRD） studies show that the annealing in Se atmosphere at 450 ℃ promotes the structural formation of CIS chalcopyrite structure.
李建庄，赵修建
摘 要：CuInSe2 （CIS） thin films were prepared by electrodeposition from the de-ionized water solution consisting of CuCl2, InCl3, H2SeO3 and Na-citrate onto Mo/soda-lime glass （SLG） substrates. A thermal processing in Se atmosphere at 450 ℃ was carried out for the electrodepositied films to improve the stoichiometry. The composition and morphology of selenized CIS thin films were studied using energy dispersive spectroscopy （EDS） and scanning electron microscopy （SEM）, respectively. X-ray diffraction （XRD） studies show that the annealing in Se atmosphere at 450 ℃ promotes the structural formation of CIS chalcopyrite structure.
关键词：