Preliminary Study to Identify Criterion for Quench Crack Prevention by Computer Simulation
来源期刊:材料热处理学报2004年第5期
论文作者:Fumiaki Ikuta Michiharu NARAZAKI Kyozo Arimoto Shigeyuki Tamura Takashi Horino Yoshio Mikita
关键词:Quench Cracking; Heat Treatment Simulation;
摘 要:A criterion for preventing quench cracks has not been established although much research has been conducted in this field. A few predictions of cracking have been recently reported using simulated results of heat treatment processes.However, these results were insufficient to predict crack generation clearly because the mechanism relates not only to stress distributions in the parts but also to material characteristics. Systematic studies by the combination of experiment and simulation are therefore required to reliably identify a criterion for crack prevention by computer simulation. As a preliminary work before starting the full-scale research, a review of quench cracking research was conducted and existing test methods were classified. Several test results for cylindrical specimens were simulated for considering a cause of the crack generation. Lastly a tentative plan was made for the future research.
Fumiaki Ikuta1,Michiharu NARAZAKI2,Kyozo Arimoto3,Shigeyuki Tamura4,Takashi Horino1,Yoshio Mikita5
(1.Neturen Co. Ltd., Kanagawa, Japan;
2.Utsunomiya University, Utsunomiya, Japan;
3.Arimotech Ltd., Osaka, Japan;
4.CRC Solutions Corp., Tokyo, Japan;
5.MIKITA Professional Engineer Office, Tokushima, Japan)
摘要:A criterion for preventing quench cracks has not been established although much research has been conducted in this field. A few predictions of cracking have been recently reported using simulated results of heat treatment processes.However, these results were insufficient to predict crack generation clearly because the mechanism relates not only to stress distributions in the parts but also to material characteristics. Systematic studies by the combination of experiment and simulation are therefore required to reliably identify a criterion for crack prevention by computer simulation. As a preliminary work before starting the full-scale research, a review of quench cracking research was conducted and existing test methods were classified. Several test results for cylindrical specimens were simulated for considering a cause of the crack generation. Lastly a tentative plan was made for the future research.