Achieving ultra-high strength friction stir welded joints of high nitrogen stainless steel by forced water cooling

来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2018年第11期

论文作者:H.Zhang D.Wang P.Xue L.H.Wu D.R.N B.L.Xiao Z.Y.Ma

文章页码:2183 - 2188

摘    要:The microstructure and properties of water-cooled and air-cooled friction stir welded(FSW) ultra-high strength high nitrogen stainless steel joints were comparatively studied. With additional rapid cooling by flowing water, the peak temperature and duration at elevated temperature during FSW were significantly reduced. Compared to those in the air-cooled joint, nugget zone with finer grains(900 nm) and heat affected zone with higher dislocation density were successfully obtained in the water-cooled joint,leading to significantly improved mechanical properties. The wear of the welding tool was significantly reduced with water cooling, resulting in better corrosion resistance during the immersion corrosion test.

详情信息展示

Achieving ultra-high strength friction stir welded joints of high nitrogen stainless steel by forced water cooling

H.Zhang1,2,D.Wang1,P.Xue1,L.H.Wu1,D.R.N1,B.L.Xiao1,Z.Y.Ma1,2

1. Shenyang National Laboratory for Materials Science,Institute of Metal Research,Chinese Academy of Sciences2. University of Chinese Academy of Sciences

摘 要:The microstructure and properties of water-cooled and air-cooled friction stir welded(FSW) ultra-high strength high nitrogen stainless steel joints were comparatively studied. With additional rapid cooling by flowing water, the peak temperature and duration at elevated temperature during FSW were significantly reduced. Compared to those in the air-cooled joint, nugget zone with finer grains(900 nm) and heat affected zone with higher dislocation density were successfully obtained in the water-cooled joint,leading to significantly improved mechanical properties. The wear of the welding tool was significantly reduced with water cooling, resulting in better corrosion resistance during the immersion corrosion test.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号