Luminescence properties of a new yellow long-lasting phosphorescence phosphor NaAlSiO4:Eu2+,Ho3+
来源期刊:JOURNAL OF RARE EARTHS2014年第9期
论文作者:庞然 赵然 贾永雷 李成宇 苏锵
文章页码:792 - 796
摘 要:A new aluminosilicate long-lasting phosphor with composition of NaAlSiO4:Eu2+,Ho3+ was synthesized and investigated. Under UV light excitation, the phosphor emitted yellow light corresponding to the characteristic emission of Eu2+ due to 5d-4f transition. Bright yellow phosphorescence sustaining for more than 30 min was observed after ceasing the excitation. The phosphorescence intensity decay obeyed a t–1 decay law, indicating a tunneling electron-hole recombination process in the phosphor. Four peaks appeared in the thermoluminescence curve and the ones at 322 and 370 K were thought to account for the long lasting phosphorescence at room temperature. The Ho3+ ion incorporated into the phosphor did not give any light but dramatically increased the intensities of both photoluminescence and phosphorescence via promoting defect levels in the phosphor.
庞然1,赵然1,2,贾永雷1,2,李成宇1,苏锵1
1. State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences2. University of the Chinese Academy of Sciences
摘 要:A new aluminosilicate long-lasting phosphor with composition of NaAlSiO4:Eu2+,Ho3+ was synthesized and investigated. Under UV light excitation, the phosphor emitted yellow light corresponding to the characteristic emission of Eu2+ due to 5d-4f transition. Bright yellow phosphorescence sustaining for more than 30 min was observed after ceasing the excitation. The phosphorescence intensity decay obeyed a t–1 decay law, indicating a tunneling electron-hole recombination process in the phosphor. Four peaks appeared in the thermoluminescence curve and the ones at 322 and 370 K were thought to account for the long lasting phosphorescence at room temperature. The Ho3+ ion incorporated into the phosphor did not give any light but dramatically increased the intensities of both photoluminescence and phosphorescence via promoting defect levels in the phosphor.
关键词: