Long Lasting Phosphorescence in Eu2+ and Ce3+ Co-Doped Strontium Borate Glasses
来源期刊：Journal of Rare Earths2006年第S1期
论文作者：张岚 李成宇 苏锵
文章页码：196 - 198
摘 要：<正>Long lasting phosphorescence （LLP） was observed in Eu2+, Ce3+ co-doped strontium borate glasses prepared under the reducing atmosphere due to the emission of both Eu2 + and Ce3+ . The methods of photoluminescence, thermolu-minescence and phosphorescence were used to study the samples, and possible mechanism was suggested. The co-doping of Ce3 + ions poisoned the phosphorescence emission of Eu2 + because of the competition to obtain the trapped electron . The phosphorescence of Ce3 + in the sample decays more quickly than that of Eu2 + , which is suggested for the reason that the emission energy of Ce3 + is higher or the distance between Ce3 + and electron traps of the glasses is longer.
张岚，李成宇，苏锵
摘 要：<正>Long lasting phosphorescence （LLP） was observed in Eu2+, Ce3+ co-doped strontium borate glasses prepared under the reducing atmosphere due to the emission of both Eu2 + and Ce3+ . The methods of photoluminescence, thermolu-minescence and phosphorescence were used to study the samples, and possible mechanism was suggested. The co-doping of Ce3 + ions poisoned the phosphorescence emission of Eu2 + because of the competition to obtain the trapped electron . The phosphorescence of Ce3 + in the sample decays more quickly than that of Eu2 + , which is suggested for the reason that the emission energy of Ce3 + is higher or the distance between Ce3 + and electron traps of the glasses is longer.
关键词：