Luminescence of emission-tunable Na15.6Ca3.84Si12O36:Ce3+,Tb3+,Na+ phosphors for near-ultraviolet light-emitting diodes
来源期刊:JOURNAL OF RARE EARTHS2016年第6期
论文作者:张佳 俞阿龙 华正和 温世正
文章页码:565 - 570
摘 要:A series of Na15.6Ca3.84Si12O36:Ce3+,Tb3+,Na+(NCS:Ce3+,Tb3+,Na+) phosphors were prepared by conventional solid-state reaction method, and their photoluminescence properties under near-ultraviolet(NUV) excitation were studied. The excitation spectrum of Ce3+-single-doped NCS showed a broad excitation band from 250 to 400 nm, which could well match with the emission wavelength of the NUV LED chip. Upon 365 nm excitation, the NCS:Ce3+,Na+ phosphor demonstrated a blue emission in the range of 400–600 nm with the predominated peak at 443 nm. By co-doping Tb3+ into NCS:0.04Ce3+,0.04Na+, tunable-emission was realized due to the energy transfer from Ce3+ to Tb3+, and nearly white light was also obtained. The investigation also revealed that warm white light could be further generated by combining the NCS:0.04Ce3+,y Tb3+,(0.04+y)Na+ with other red-emitting phosphors. Thus, the NCS:Ce3+,Tb3+,Na+ phosphors could be promising candidate for white LEDs.
张佳1,2,俞阿龙1,2,华正和1,2,温世正1,2
1. School of Physics and Electronic Electrical Engineering Huaiyin Normal University2. Jiangsu Provincial Key Laboratory of Modern Measurement Technology and Intelligent System
摘 要:A series of Na15.6Ca3.84Si12O36:Ce3+,Tb3+,Na+(NCS:Ce3+,Tb3+,Na+) phosphors were prepared by conventional solid-state reaction method, and their photoluminescence properties under near-ultraviolet(NUV) excitation were studied. The excitation spectrum of Ce3+-single-doped NCS showed a broad excitation band from 250 to 400 nm, which could well match with the emission wavelength of the NUV LED chip. Upon 365 nm excitation, the NCS:Ce3+,Na+ phosphor demonstrated a blue emission in the range of 400–600 nm with the predominated peak at 443 nm. By co-doping Tb3+ into NCS:0.04Ce3+,0.04Na+, tunable-emission was realized due to the energy transfer from Ce3+ to Tb3+, and nearly white light was also obtained. The investigation also revealed that warm white light could be further generated by combining the NCS:0.04Ce3+,y Tb3+,(0.04+y)Na+ with other red-emitting phosphors. Thus, the NCS:Ce3+,Tb3+,Na+ phosphors could be promising candidate for white LEDs.
关键词: