Rheological behavior and constitutive equations of heterogeneous titanium-bearing molten slag
来源期刊:International Journal of Minerals Metallurgy and Materials2015年第8期
论文作者:Tao Jiang De-ming Liao Mi Zhou Qiao-yi Zhang Hong-rui Yue Song-tao Yang Pei-ning Duan Xiang-xin Xue
文章页码:804 - 810
摘 要:Experimental studies on the rheological properties of a Ca O–Si O2–Al2O3–Mg O–Ti O2–(Ti C) blast furnace(BF) slag system were conducted using a high-temperature rheometer to reveal the non-Newtonian behavior of heterogeneous titanium-bearing molten slag. By measuring the relationships among the viscosity, the shear stress and the shear rate of molten slags with different Ti C contents at different temperatures, the rheological constitutive equations were established along with the rheological parameters; in addition, the non-Newtonian fluid types of the molten slags were determined. The results indicated that, with increasing Ti C content, the viscosity of the molten slag tended to increase. If the Ti C content was less than 2wt%, the molten slag exhibited the Newtonian fluid behavior when the temperature was higher than the critical viscosity temperature of the molten slag. In contrast, the molten slag exhibited the non-Newtonian pseudoplastic fluid characteristic and the shear thinning behavior when the temperature was less than the critical viscosity temperature. However, if the Ti C content exceeded 4wt%, the molten slag produced the yield stress and exhibited the Bingham and plastic pseudoplastic fluid behaviors when the temperature was higher and lower than the critical viscosity temperature, respectively. When the Ti C content increased further, the yield stress of the molten slag increased and the shear thinning phenomenon became more obvious.
Tao Jiang1,2,De-ming Liao1,Mi Zhou1,Qiao-yi Zhang1,Hong-rui Yue1,Song-tao Yang1,Pei-ning Duan1,2,Xiang-xin Xue1,2
1. School of Materials and Metallurgy, Northeastern University2. Liaoning Key Laboratory for Recycling Science of Metallurgical Resources
摘 要:Experimental studies on the rheological properties of a Ca O–Si O2–Al2O3–Mg O–Ti O2–(Ti C) blast furnace(BF) slag system were conducted using a high-temperature rheometer to reveal the non-Newtonian behavior of heterogeneous titanium-bearing molten slag. By measuring the relationships among the viscosity, the shear stress and the shear rate of molten slags with different Ti C contents at different temperatures, the rheological constitutive equations were established along with the rheological parameters; in addition, the non-Newtonian fluid types of the molten slags were determined. The results indicated that, with increasing Ti C content, the viscosity of the molten slag tended to increase. If the Ti C content was less than 2wt%, the molten slag exhibited the Newtonian fluid behavior when the temperature was higher than the critical viscosity temperature of the molten slag. In contrast, the molten slag exhibited the non-Newtonian pseudoplastic fluid characteristic and the shear thinning behavior when the temperature was less than the critical viscosity temperature. However, if the Ti C content exceeded 4wt%, the molten slag produced the yield stress and exhibited the Bingham and plastic pseudoplastic fluid behaviors when the temperature was higher and lower than the critical viscosity temperature, respectively. When the Ti C content increased further, the yield stress of the molten slag increased and the shear thinning phenomenon became more obvious.
关键词: