Study on Interface Structure and Bond Properties between Cemented Carbide and Tool Steel Blazing with amorphous alloy
来源期刊:材料热处理学报2004年第5期
论文作者:XU Jin-fu ZOU Gui-sheng Xu Xue-bo Huang Geng-hua
关键词:Ni-base alloy; blazing; cemented carbide; tool steel; dynamics thermodynamics analoque testing machine;
摘 要:Cemented Carbide YG11C and Tool Steel Crl2MoV was blazed with Ni-base amorphous alloys, QG-1011,MBF-20 and MBF-75, using dynamics thermodynamics analogue testing machine Gleeble 1500D. The effects of brazing temperature, holding time and holding pressure on micro-structure and bond strength were investigated. Results showed that YG11C and Cr12MoV were all wetted well by these three Ni-base alloys, and the bond strength was as high as 220MPa,320MPa, 320MPa respectively. When the blazing temperature was at the point over the melting point 60-70℃ of Ni-base alloy, the holding time was about 2-10min, the suitable pressure was benefit for improving the brazing quality.Microanalysis showed Co in cemented carbide diffused into liquid brazing alloy and formed the Fe-Co solid .solution.
XU Jin-fu1,BAO Ming-dong2,ZOU Gui-sheng3,Xu Xue-bo1,Huang Geng-hua3
(1.Research Institute of Materials & Technology, Ningbo College, Ningbo315016, China;
2.State key laboratory for Mechanical Behavior of Materials, Xi'an Jiaotong University, Xi'an, 710049 China;
3.Department of Mechanical Engineering, Tsinghua University, Beijing 100084 China)
摘要:Cemented Carbide YG11C and Tool Steel Crl2MoV was blazed with Ni-base amorphous alloys, QG-1011,MBF-20 and MBF-75, using dynamics thermodynamics analogue testing machine Gleeble 1500D. The effects of brazing temperature, holding time and holding pressure on micro-structure and bond strength were investigated. Results showed that YG11C and Cr12MoV were all wetted well by these three Ni-base alloys, and the bond strength was as high as 220MPa,320MPa, 320MPa respectively. When the blazing temperature was at the point over the melting point 60-70℃ of Ni-base alloy, the holding time was about 2-10min, the suitable pressure was benefit for improving the brazing quality.Microanalysis showed Co in cemented carbide diffused into liquid brazing alloy and formed the Fe-Co solid .solution.