Comparison effects of lanthanum stearate and antioxidants in epoxidized natural rubber
来源期刊:JOURNAL OF RARE EARTHS2015年第11期
论文作者:杨昌金 罗勇悦 彭政 许逵 钟杰平
文章页码:1236 - 1240
摘 要:This work studied possibilities of using lanthanum stearate(LaS t) as an antioxidant in epoxidized natural rubber containing 25 mol.% expoxidation(ENR25) compounds. For comparison purposes, two commercial antioxidant 4010 NA and MB were also used. The influence of LaS t, antioxidant 4010 NA and MB on cure characteristics, mechanical properties, crosslink density, hot air aging and thermo-oxidative degradation were studied. The results indicated that the incorporation of LaS t and antioxidants could accelerate the vulcanization of ENR. The ENR vulcanizates with antioxidant MB had better mechanical properties than 4010 NA and LaS t. Compared with antioxidant 4010 NA and MB, the ENR25 vulcanizates with the addition of LaS t exhibited the best hot air aging resistance and thermo-oxidative stability.
杨昌金1,罗勇悦1,彭政1,许逵1,2,钟杰平3
1. Chinese Agricultural Ministry Key Laboratory of Tropical Crop Product Processing, Agricultural Product Processing Research Institute, Chinese Academy of Tropical Agricultural Sciences2. Rubber Research Institute, Chinese Academy of Tropical Agricultural Sciences3. School of Science, Guangdong Ocean University
摘 要:This work studied possibilities of using lanthanum stearate(LaS t) as an antioxidant in epoxidized natural rubber containing 25 mol.% expoxidation(ENR25) compounds. For comparison purposes, two commercial antioxidant 4010 NA and MB were also used. The influence of LaS t, antioxidant 4010 NA and MB on cure characteristics, mechanical properties, crosslink density, hot air aging and thermo-oxidative degradation were studied. The results indicated that the incorporation of LaS t and antioxidants could accelerate the vulcanization of ENR. The ENR vulcanizates with antioxidant MB had better mechanical properties than 4010 NA and LaS t. Compared with antioxidant 4010 NA and MB, the ENR25 vulcanizates with the addition of LaS t exhibited the best hot air aging resistance and thermo-oxidative stability.
关键词: