Optimum rolling speed and relevant temperature-and reduction-dependent interfacial friction behavior during the break-down rolling of AZ31B alloy
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2018年第11期
论文作者：Weitao Jia Yan Tang Fangkun Ning Qichi Le Lei Bao
文章页码：2051 - 2062
摘 要：The present study aimed to determine the optimum rolling speed for break-down rolling of as-cast AZ31 B alloy and investigated the friction behavior associated with temperature-and reduction-sensitivity at the roll/plate contact interface. Tensile testing, formability evaluation and microstructural studies relevant to different rolling speeds were performed and finally the optimum operating rolling speed（50.0 ± 0.8 m/min） was obtained. Further, the effects of rolling reduction and initial temperature were assessed on the temperature variation, lateral spread and interfacial friction behavior at optimum rolling speed. The results showed that lower rolling speed（18.0 ± 0.8 m/min） resulted in an incompletely recrystallized structure where twins occupied relatively high volume fraction. Twinning dominated the deformation at rolling speed exceeding the optimum, resulting in the local recrystallization with shear bands and coarse grains. Rolling at 50.0 ± 0.8 m/min could get the best overall tensile properties and rolling formability due to the relatively high recrystallization degree and microstructure uniformity. An inverse method has been developed to determine the interfacial friction coefficient during interaction of AZ31 B alloy with roll surfaces. When rolling at the optimum speed, the interfacial friction coefficient ranged from 0.16 to 0.58, which was strongly positively correlated with the reduction but slightly positively correlated with the initial temperature. Depended on the rolling characteristics, external friction effect coefficient ranged from 1.25 to 2.35 and it exhibited positive correlation with both the initial rolling temperature and rolling reduction.
Weitao Jia1，Yan Tang1，Fangkun Ning1，Qichi Le1，Lei Bao1,2
1. Key Laboratory of Electromagnetic Processing of Materials,Ministry of Education,Northeastern University2. Key Laboratory of Superlight Materials & Surface Technology,Ministry of Education,Harbin Engineering University
摘 要：The present study aimed to determine the optimum rolling speed for break-down rolling of as-cast AZ31 B alloy and investigated the friction behavior associated with temperature-and reduction-sensitivity at the roll/plate contact interface. Tensile testing, formability evaluation and microstructural studies relevant to different rolling speeds were performed and finally the optimum operating rolling speed（50.0 ± 0.8 m/min） was obtained. Further, the effects of rolling reduction and initial temperature were assessed on the temperature variation, lateral spread and interfacial friction behavior at optimum rolling speed. The results showed that lower rolling speed（18.0 ± 0.8 m/min） resulted in an incompletely recrystallized structure where twins occupied relatively high volume fraction. Twinning dominated the deformation at rolling speed exceeding the optimum, resulting in the local recrystallization with shear bands and coarse grains. Rolling at 50.0 ± 0.8 m/min could get the best overall tensile properties and rolling formability due to the relatively high recrystallization degree and microstructure uniformity. An inverse method has been developed to determine the interfacial friction coefficient during interaction of AZ31 B alloy with roll surfaces. When rolling at the optimum speed, the interfacial friction coefficient ranged from 0.16 to 0.58, which was strongly positively correlated with the reduction but slightly positively correlated with the initial temperature. Depended on the rolling characteristics, external friction effect coefficient ranged from 1.25 to 2.35 and it exhibited positive correlation with both the initial rolling temperature and rolling reduction.
关键词：