Research Progress in Solderable Black Pad of Electroless Nickel/Immersion Gold
来源期刊：Journal of Rare Earths2007年第S2期
论文作者：刘海萍 李宁 毕四富 黎德育
文章页码：308 - 312
摘 要：Electroless nickel/immersion gold (ENIG) technology is widely used as one of the surface final finish for electronics packaging substrate and printed circuit board (PCB), providing a protective, conductive and solderable surface. However, there is a solder joint interfacial brittle fracture (or solderability failure) of using the ENIG coating. The characteristics and the application of ENIG technology were narrated in this paper. The research progress on the solderability failure of ENIG was introduced. The mechanism of "black pad" and the possible measure of eliminating or alleviating the "black pad" were also introduced. The development direction and market prospects of ENIG were prospected.
刘海萍，李宁，毕四富，黎德育
摘 要：Electroless nickel/immersion gold (ENIG) technology is widely used as one of the surface final finish for electronics packaging substrate and printed circuit board (PCB), providing a protective, conductive and solderable surface. However, there is a solder joint interfacial brittle fracture (or solderability failure) of using the ENIG coating. The characteristics and the application of ENIG technology were narrated in this paper. The research progress on the solderability failure of ENIG was introduced. The mechanism of "black pad" and the possible measure of eliminating or alleviating the "black pad" were also introduced. The development direction and market prospects of ENIG were prospected.
关键词：