人造金红石母液净化制取软磁氧化铁粉研究
来源期刊：钢铁钒钛2010年第4期
论文作者：王彦华 梁英
文章页码：92 - 97
关键词：人造金红石母液； 除杂； 正交试验； 软磁用氧化铁粉
Key words：synthetic rutile mother liquor； removal of impurities； orthogonal test； ferric oxide powder for soft-magnetic
摘 要：针对人造金红石母液中影响材料磁性能的硅、铝、钙、镁杂质存在形态,采取控制溶液pH值,添加除杂沉淀剂的方法,通过正交试验和验证试验,获得wSiO<sub>2</sub>≤16.7×10-6、wCaO<5×10-6、wMgO<5×10-6、wAl<sub>2</sub>O<sub>3</sub><10×10-6的净化溶液,焙烧获得的氧化铁粉达到软磁用氧化铁粉标准SJ/T10383-1993 YHT2水平。
Abstract: An investigation was made into the form of impurities like silicon,aluminum,calcium and magnesium present in the synthetic rutile mother liquor,which have some effects on the magnetic property of materials.By controlling pH value of the liquor and adding precipitation agent,a purified solution containing wSiO<sub>2</sub>≤16.7×10-6、wCaO<5×10-6、wMgO<5×10-6、wAl<sub>2</sub>O<sub>3</sub><10×10-6 was obtained based on orthogonal and validation tests.Then the purified solution was roasted to prepare ferric oxide powder for soft-magnetic use which is consistent with the standard SJ/T10383-1993YHT2.
王彦华1，梁英2
(1.攀钢集团研究院有限公司，四川成都 611731
2.攀枝花钢钒有限公司 冷轧厂，四川攀枝花 617023)
摘 要：针对人造金红石母液中影响材料磁性能的硅、铝、钙、镁杂质存在形态,采取控制溶液pH值,添加除杂沉淀剂的方法,通过正交试验和验证试验,获得wSiO<sub>2</sub>≤16.7×10-6、wCaO<5×10-6、wMgO<5×10-6、wAl<sub>2</sub>O<sub>3</sub><10×10-6的净化溶液,焙烧获得的氧化铁粉达到软磁用氧化铁粉标准SJ/T10383-1993 YHT2水平。
关键词：人造金红石母液； 除杂； 正交试验； 软磁用氧化铁粉