Microstructure and compressive properties of INCO-617 alloy hollow sphere foam
来源期刊：Rare Metals2007年第S1期
论文作者：LI Zhiwei,WEI Zunjie,WANG Hongwei,and ZHU Zhaojun School of Materials Science and Engineering,Harbin Institute of Technology,Harbin ,China
文章页码：129 - 133
摘 要：INCO-617 alloy hollow sphere foams with average aperture of about 3 mm and about 0.12 mm wall thickness were fabricated by hollow sphere method.Firstly the wet spheres,which are formed as powder shells from slurry by coating polystyrene balls,were arranged with body-centered cubic（BCC） structure.Subsequently,the sphere stacks were heat-treated in vacuum at 350 ℃ for 40 min to decompose the organic materials,and sintered at different temperatures for different time.The effects of slurry components,sintering temperature and sintering time on the density and porosity of cell wall of hollow sphere foam were studied through Scanning Electron Microscopy.The results show that the densities of INCO-617 alloy hollow sphere foam,increasing with the increase of powder content in slurry,sintering temperature and sintering time,range from 1.112 to 1.216 g·cm-3.Extension of sintering time can reduce the porosity of cell wall,which enhances the compression strength of hollow sphere foam significantly.
LI Zhiwei,WEI Zunjie,WANG Hongwei,and ZHU Zhaojun School of Materials Science and Engineering,Harbin Institute of Technology,Harbin 150001,China
摘 要：INCO-617 alloy hollow sphere foams with average aperture of about 3 mm and about 0.12 mm wall thickness were fabricated by hollow sphere method.Firstly the wet spheres,which are formed as powder shells from slurry by coating polystyrene balls,were arranged with body-centered cubic（BCC） structure.Subsequently,the sphere stacks were heat-treated in vacuum at 350 ℃ for 40 min to decompose the organic materials,and sintered at different temperatures for different time.The effects of slurry components,sintering temperature and sintering time on the density and porosity of cell wall of hollow sphere foam were studied through Scanning Electron Microscopy.The results show that the densities of INCO-617 alloy hollow sphere foam,increasing with the increase of powder content in slurry,sintering temperature and sintering time,range from 1.112 to 1.216 g·cm-3.Extension of sintering time can reduce the porosity of cell wall,which enhances the compression strength of hollow sphere foam significantly.
关键词：