Microwave-Assisted Synthesis of LaPO4∶Ce, Tb and Phosphor Characterizations
来源期刊：Journal of Rare Earths2007年第S1期
论文作者：董丽敏 张耀明 吴泽 赵元 韩志东 张显友
文章页码：286 - 289
摘 要：A novel method was devised to prepare green phosphor of LaPO4∶Ce, Tb by the combination of co-precipitation and microwave irradiation. The effective hess of microwave as pre-treated process and after process and microwave irradiation time were mainly discussed. The formation process and structure of green phosphor of LaPO4∶Ce, Tb were characterized by TG-DTA, XRD and SEM, respectively. As a result, phosphor of monoclinic structure with widely distributed particle size about 70 nm was successfully synthesized. The effect of microwave-assisted method as pretreatment and after-treatment on the structure and luminescent was studied property. Results indicate that the after-treatment by microwave would enhance the crystallinity as well as fluorescence intensity, the fluorescence intensity increased with the time of microwave pretreatment time, the high fluorescence intensity was found at 80 min pretreatment time. Morphological structure of phosphor particles prepared by two methods seemed similar. The emission spectrum and excitation spectrum of phosphor as prepared detected by spectrophotometer showed typical luminescent of green phosphor, the luminescence mechanism was preliminarily discussed.
董丽敏，张耀明，吴泽，赵元，韩志东，张显友
摘 要：A novel method was devised to prepare green phosphor of LaPO4∶Ce, Tb by the combination of co-precipitation and microwave irradiation. The effective hess of microwave as pre-treated process and after process and microwave irradiation time were mainly discussed. The formation process and structure of green phosphor of LaPO4∶Ce, Tb were characterized by TG-DTA, XRD and SEM, respectively. As a result, phosphor of monoclinic structure with widely distributed particle size about 70 nm was successfully synthesized. The effect of microwave-assisted method as pretreatment and after-treatment on the structure and luminescent was studied property. Results indicate that the after-treatment by microwave would enhance the crystallinity as well as fluorescence intensity, the fluorescence intensity increased with the time of microwave pretreatment time, the high fluorescence intensity was found at 80 min pretreatment time. Morphological structure of phosphor particles prepared by two methods seemed similar. The emission spectrum and excitation spectrum of phosphor as prepared detected by spectrophotometer showed typical luminescent of green phosphor, the luminescence mechanism was preliminarily discussed.
关键词：