Efects of Molybdenum Concentration and Valence State on the Structural and Magnetic Properties of BaFe11.6MoxZn0.4-xO19 Hexaferrites

来源期刊:Acta Metallurgica Sinica2013年第5期

论文作者:G.H.Dushaq S.H.Mahmood I.Bsoul H.K.Juwhari B.Lahlouh M.A.AlDamen

文章页码:509 - 516

摘    要:Barium hexaferrites BaFe11.6Mox Zn0.4-x O19(x=0.1,0.2,0.4)were prepared by precipitation of the precursors using wet chemical mixture method and then sintering the dried powders at 1100℃ .The properties of the prepared samples were investigated using X-ray difraction(XRD),scanning electron microscopy(SEM),vibrating sample magnetometer,and Mssbauer spectroscopy.XRD patterns revealed that all prepared samples had BaFe12O19hexaferrite structure as a majority phase.SEM images demonstated that the samples consisted mainly of hexagonal platelet-like grains with diameters ranging from 100 to 500 nm.Mssbauer spectra revealed that Zn2+ions occupy 4f1 sites leading to the splitting of the 12k component.However Mo6+ions occupy 2b sites while Mo4+ prefer 4f1 and 12k sites.For the sample with x=0.4,Mo6+and Mo4+ ions were found to have preference for 2b and 12k sites,respectively,and to induce the development of Fe2+ions in the hexaferrite,leading to noticeable changes in the magnetic properties of the system.The observed magnetic properties were found to be consistent with the preferential site occupation of metal ions,and the hyperfine fields derived from Mssbauer spectra of these samples.

详情信息展示

Efects of Molybdenum Concentration and Valence State on the Structural and Magnetic Properties of BaFe11.6MoxZn0.4-xO19 Hexaferrites

G.H.Dushaq1,S.H.Mahmood1,I.Bsoul2,H.K.Juwhari1,B.Lahlouh1,M.A.AlDamen3

1. Physics Department, The University of Jordan2. Physics Department, Al al-Bayt University3. Chemistry Department, The University of Jordan

摘 要:Barium hexaferrites BaFe11.6Mox Zn0.4-x O19(x=0.1,0.2,0.4)were prepared by precipitation of the precursors using wet chemical mixture method and then sintering the dried powders at 1100℃ .The properties of the prepared samples were investigated using X-ray difraction(XRD),scanning electron microscopy(SEM),vibrating sample magnetometer,and Mssbauer spectroscopy.XRD patterns revealed that all prepared samples had BaFe12O19hexaferrite structure as a majority phase.SEM images demonstated that the samples consisted mainly of hexagonal platelet-like grains with diameters ranging from 100 to 500 nm.Mssbauer spectra revealed that Zn2+ions occupy 4f1 sites leading to the splitting of the 12k component.However Mo6+ions occupy 2b sites while Mo4+ prefer 4f1 and 12k sites.For the sample with x=0.4,Mo6+and Mo4+ ions were found to have preference for 2b and 12k sites,respectively,and to induce the development of Fe2+ions in the hexaferrite,leading to noticeable changes in the magnetic properties of the system.The observed magnetic properties were found to be consistent with the preferential site occupation of metal ions,and the hyperfine fields derived from Mssbauer spectra of these samples.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号