Effect of Curing Temperature on Tunnel Fire Insulation of Aerogel Cement Paste Coatings

来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2021年第1期

论文作者:王新杰 XU Donghang 朱平华 CHEN Chunhong QIAN Zhongqiu

文章页码:93 - 102

摘    要:To further strengthen the protective effect of aerogel cement paste (ACP) coating on self-compacting concrete (SCC) in tunnel fire under the optimal mix proportion,the effect of curing temperature (from 5 to 80 ℃,based on site construction curing temperature and surrounding rock temperature) on fire insulation of ACP was investigated.The mechanical properties,thermal conductivity and porosity of ACP were tested.The microstructure of ACP was characterized by means of SEM,XRD and TG/DTG.The results reveal that 50 ℃ is the optimal curing temperature for ACP with good mechanical properties and fire insulation.Relatively high curing temperature can facilitate hydration and pozzolanic reactions,contributing to the generation of more stable substances (such as C-S-H gels,tobermorite and thenardite,etc).ACP under excessive low curing temperature brings inhomogeneous microstructure with coarse pores,leading to producing wider and longer microcracks when it is exposed to tunnel fire.The microcracks make the heat convection and thermal radiation more significant and thus accelerate the damage of ACP under fire.In case of the less than 7% difference of thermal conductivity,dense microstructure and stable substances are more conducive to strengthening fire insulation of ACP.In practical engineering applications,the thickness of protective layer of ACP can be further optimized when ACP is cured under about 50 ℃.

详情信息展示

Effect of Curing Temperature on Tunnel Fire Insulation of Aerogel Cement Paste Coatings

王新杰1,XU Donghang1,朱平华1,CHEN Chunhong1,QIAN Zhongqiu2

1. Department of Civil Engineering, Changzhou University2. Architectural Research Institute Group Co., Ltd.

摘 要:To further strengthen the protective effect of aerogel cement paste (ACP) coating on self-compacting concrete (SCC) in tunnel fire under the optimal mix proportion,the effect of curing temperature (from 5 to 80 ℃,based on site construction curing temperature and surrounding rock temperature) on fire insulation of ACP was investigated.The mechanical properties,thermal conductivity and porosity of ACP were tested.The microstructure of ACP was characterized by means of SEM,XRD and TG/DTG.The results reveal that 50 ℃ is the optimal curing temperature for ACP with good mechanical properties and fire insulation.Relatively high curing temperature can facilitate hydration and pozzolanic reactions,contributing to the generation of more stable substances (such as C-S-H gels,tobermorite and thenardite,etc).ACP under excessive low curing temperature brings inhomogeneous microstructure with coarse pores,leading to producing wider and longer microcracks when it is exposed to tunnel fire.The microcracks make the heat convection and thermal radiation more significant and thus accelerate the damage of ACP under fire.In case of the less than 7% difference of thermal conductivity,dense microstructure and stable substances are more conducive to strengthening fire insulation of ACP.In practical engineering applications,the thickness of protective layer of ACP can be further optimized when ACP is cured under about 50 ℃.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号