Influence of coating on the photoluminescence of Tb3+ doped ZnS e/ZnS core-shell quantum dots
来源期刊:JOURNAL OF RARE EARTHS2016年第8期
论文作者:J.Cichos M.Karbowiak D.Hreniak W.Str?k
文章页码:828 - 832
摘 要:Tb3+-doped ZnSe and ZnSe/ZnS nanocrystals were synthesized using modified hot-injection method.The observation of the characteristic quantum dots absorption features in a time-gated excitation spectrum was recorded while monitoring Tb3+ emission at 545 nm provided direct evidence for successful incorporation of dopant ions into semiconductor host.Relatively long decay time(1.5 ms) of Tb3+ emission indicated that dopant ions were well protected from interaction with surface ligands.Emission properties of core ZnSe:Tb3+ nanocrystals were only slightly modified upon growth of ZnS shell..
J.Cichos1,M.Karbowiak1,D.Hreniak2,W.Str?k2
1. Faculty of Chemistry, University of Wroc?aw, ul. F.2. Institute of Low Temperature and Structure Research,Polish Academy of Sciences
摘 要:Tb3+-doped ZnSe and ZnSe/ZnS nanocrystals were synthesized using modified hot-injection method.The observation of the characteristic quantum dots absorption features in a time-gated excitation spectrum was recorded while monitoring Tb3+ emission at 545 nm provided direct evidence for successful incorporation of dopant ions into semiconductor host.Relatively long decay time(1.5 ms) of Tb3+ emission indicated that dopant ions were well protected from interaction with surface ligands.Emission properties of core ZnSe:Tb3+ nanocrystals were only slightly modified upon growth of ZnS shell..
关键词: