Researches on preparation and properties of polypropylene nonwovens containing rare earth luminous materials
来源期刊：JOURNAL OF RARE EARTHS2014年第12期
论文作者：余媛 王建 朱亚楠 葛明桥
文章页码：1196 - 1200
摘 要：Polypropylene composite nonwovens containing rare-earth strontium aluminates Sr Al2O4:Eu2+,Dy3+ and functional additives were fabricated by the spun-bonded technique.The optical properties, morphology and mechanical properties of the samples were characterized.Results from scanning electron microscopy photographs（SEM） indicated that the surface of the fiber was destroyed by the addition of rare earth luminescent materials lightly but the thickness of the fiber was uniform.Differential scanning calorimetry results showed that pure polypropylene has the double crystallization peak at 162.3 and 165.1 °C.Studies from X-ray diffraction showed that the nonwoven prepared with the luminescent materials contained the α-monoclinic crystal and β crystalline phase.Furthermore, the afterglow properties were tested, which showed that the afterglow curve of the luminous nonwoven was similar to that of strontium aluminate, and the intensity was more intensive than luminous nonwoven at the beginning.The nonwoven fabricated with the luminescent material did not affect the crystal lattice of the polymer making the materials have potential applications in fluorescent lamps and field emission displays（FEDs）.
余媛，王建，朱亚楠，葛明桥
Key Laboratory of Eco-Textile of Ministry of Education, College of Textiles and Clothing, Jiangnan University
摘 要：Polypropylene composite nonwovens containing rare-earth strontium aluminates Sr Al2O4:Eu2+,Dy3+ and functional additives were fabricated by the spun-bonded technique.The optical properties, morphology and mechanical properties of the samples were characterized.Results from scanning electron microscopy photographs（SEM） indicated that the surface of the fiber was destroyed by the addition of rare earth luminescent materials lightly but the thickness of the fiber was uniform.Differential scanning calorimetry results showed that pure polypropylene has the double crystallization peak at 162.3 and 165.1 °C.Studies from X-ray diffraction showed that the nonwoven prepared with the luminescent materials contained the α-monoclinic crystal and β crystalline phase.Furthermore, the afterglow properties were tested, which showed that the afterglow curve of the luminous nonwoven was similar to that of strontium aluminate, and the intensity was more intensive than luminous nonwoven at the beginning.The nonwoven fabricated with the luminescent material did not affect the crystal lattice of the polymer making the materials have potential applications in fluorescent lamps and field emission displays（FEDs）.
关键词：