Optimization of the Content of Tricalcium Silicate of High Cementing Clinker
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第3期
论文作者：陈琳 沈晓冬
文章页码：578 - 582
摘 要：Optimization of the content of tricalcium silicate（C 3 S）of high cementing clinker was investigated.The content of free-CaO（f-CaO）,mineral composite,the content of C 3 S in the clinker and the hydration product were analyzed by chemical analysis and X-ray diffraction（XRD）."K Value"method of QXRD was selected as a quantitative analysis way to measure the content of C 3 S,and the strength of cement paste was determined.The results show that at a water cement ratio of 0.29,the strength of cement paste with 73%C 3 S can be up to 97.5 MPa at 28 days age.The strength at 28 d of cement with 73%C 3 S is 16%higher than that with 78%C 3 S at water requirement for normal consistency.The relationship between the strength of high cementing Portland cement and the content of C 3 S in the clinker is nonlinear.According to the strength of cement paste,the optimal content of C 3 S in cement clinker is around 73%in this paper.
陈琳1,2，沈晓冬1
1. State Key Laboratory of Materials-oriented Chemical Engineering,College of Materials Science and Engineering,Nanjing University of Technology2. Department of Civil Engineering,Nanjing Technical Vocational College
摘 要：Optimization of the content of tricalcium silicate（C 3 S）of high cementing clinker was investigated.The content of free-CaO（f-CaO）,mineral composite,the content of C 3 S in the clinker and the hydration product were analyzed by chemical analysis and X-ray diffraction（XRD）."K Value"method of QXRD was selected as a quantitative analysis way to measure the content of C 3 S,and the strength of cement paste was determined.The results show that at a water cement ratio of 0.29,the strength of cement paste with 73%C 3 S can be up to 97.5 MPa at 28 days age.The strength at 28 d of cement with 73%C 3 S is 16%higher than that with 78%C 3 S at water requirement for normal consistency.The relationship between the strength of high cementing Portland cement and the content of C 3 S in the clinker is nonlinear.According to the strength of cement paste,the optimal content of C 3 S in cement clinker is around 73%in this paper.
关键词：