Synthesis and Characterization of Bimodal Mesoporous Silica
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2012年第6期
论文作者：张晓芳 郭翠梨
文章页码：1084 - 1088
摘 要：Mesoporous silica with controllable bimodal pore size distribution was synthesized with cetyltrimethylammonium bromide （CTAB） as chemical template for small mesopores and silica gel as physical template for large mesopores. The structure of synthesized samples were characterized by Fourier transform infrared （FT-IR） spectroscopy, X-ray diffraction （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and N2 adsorption-desorption measurements. The experimental results show that bimodal mesoporous silica consists of small mesopores of about 3 nm and large mesopores of about 45 nm. The small mesopores which were formed on the external surface and pore walls of the silica gel had similar characters with those of MCM-41, while large mesopores were inherited from parent silica gel material. The pore size distribution of the synthesized silica can be adjusted by changing the relative content of TEOS and silica gel or the feeding sequence of silica gel and NH4OH.
张晓芳，郭翠梨
School of Chemical Engineering and Technology, Tianjin University
摘 要：Mesoporous silica with controllable bimodal pore size distribution was synthesized with cetyltrimethylammonium bromide （CTAB） as chemical template for small mesopores and silica gel as physical template for large mesopores. The structure of synthesized samples were characterized by Fourier transform infrared （FT-IR） spectroscopy, X-ray diffraction （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and N2 adsorption-desorption measurements. The experimental results show that bimodal mesoporous silica consists of small mesopores of about 3 nm and large mesopores of about 45 nm. The small mesopores which were formed on the external surface and pore walls of the silica gel had similar characters with those of MCM-41, while large mesopores were inherited from parent silica gel material. The pore size distribution of the synthesized silica can be adjusted by changing the relative content of TEOS and silica gel or the feeding sequence of silica gel and NH4OH.
关键词：