Fabrication of aluminum matrix composite reinforced with carbon nanotubes
来源期刊：Rare Metals2007年第5期
论文作者：DENG Chunfeng,),ZHANG Xuexi),MA Yanxia),and WANG Dezun) ) School of Materials Science and Engineering,Harbin Institute of Technology,Harbin ,China ) Luoyang Ship Material Research Institute,Luoyang ,China
文章页码：450 - 455
摘 要：1.0wt.% carbon nanotube （CNT） reinforced 2024Al matrix composite was fabricated by cold isostatic press and subsequent hot extrusion techniques. The mechanical properties of the composite were measured by a tensile test. Mean-while,the fracture surfaces were examined using field emission scanning electron microscopy. The experimental results show that CNTs are dispersed homogeneously in the composite and that the interfaces of the Al matrix and the CNT bond well. Although the tensile strength and the Young’s modulus of the composite are enhanced markedly,the elongation does not decrease when compared with the matrix material fabricated under the same process. The reasons for the increments may be the extraordinary mechanical properties of CNTs,and the bridging and pulling-out role of CNTs in the Al matrix composite.
摘要：1.0wt.% carbon nanotube （CNT） reinforced 2024Al matrix composite was fabricated by cold isostatic press and subsequent hot extrusion techniques. The mechanical properties of the composite were measured by a tensile test. Mean-while,the fracture surfaces were examined using field emission scanning electron microscopy. The experimental results show that CNTs are dispersed homogeneously in the composite and that the interfaces of the Al matrix and the CNT bond well. Although the tensile strength and the Young’s modulus of the composite are enhanced markedly,the elongation does not decrease when compared with the matrix material fabricated under the same process. The reasons for the increments may be the extraordinary mechanical properties of CNTs,and the bridging and pulling-out role of CNTs in the Al matrix composite.
关键词：