Optimized use of MgO flux in the agglomeration of high-chromium vanadium–titanium magnetite
来源期刊：International Journal of Minerals Metallurgy and Materials2015年第4期
论文作者：Jue Tang Man-sheng Chu Xiang-xin Xue
文章页码：371 - 380
摘 要：The optimized use of Mg O flux in the agglomeration of high-chromium vanadium–titanium magnetite was investigated systematically through sinter and pellet experiments. Mg O was added in the form of magnesite. When the content of Mg O in the sinter was increased from 1.95wt% to 2.63wt%, the low-temperature reduction degradation index increased from 80.57% to 82.71%. When the content of Mg O in the pellet was increased from 1.14wt% to 2.40wt%, the reduction swelling index decreased from 15.2% to 8.6%; however, the compressive strength of the oxidized pellet decreased dramatically and it was 1985 N with an Mg O content of 1.14wt%. This compressive strength does not satisfy the requirements for blast-furnace production. When all of the aforementioned results were taken into account, the sinter with a high Mg O content（2.63wt%） matching the pellet with a low Mg O content（less than 1.14wt%） was the rational burden structure for smelting high-chromium vanadium–titanium magnetite in blast furnaces.
Jue Tang，Man-sheng Chu，Xiang-xin Xue
School of Material and Metallurgy, Northeastern University
摘 要：The optimized use of Mg O flux in the agglomeration of high-chromium vanadium–titanium magnetite was investigated systematically through sinter and pellet experiments. Mg O was added in the form of magnesite. When the content of Mg O in the sinter was increased from 1.95wt% to 2.63wt%, the low-temperature reduction degradation index increased from 80.57% to 82.71%. When the content of Mg O in the pellet was increased from 1.14wt% to 2.40wt%, the reduction swelling index decreased from 15.2% to 8.6%; however, the compressive strength of the oxidized pellet decreased dramatically and it was 1985 N with an Mg O content of 1.14wt%. This compressive strength does not satisfy the requirements for blast-furnace production. When all of the aforementioned results were taken into account, the sinter with a high Mg O content（2.63wt%） matching the pellet with a low Mg O content（less than 1.14wt%） was the rational burden structure for smelting high-chromium vanadium–titanium magnetite in blast furnaces.
关键词：