Facile synthesis, morphology and structure of Dy2O3 nanoparticles through electrochemical precipitation
来源期刊：Rare Metals2016年第8期
论文作者：Taher Yousefi Meisam Torab-Mostaedi Abolfazl Aghaei Hossein Ghasemi-Mobtaker
文章页码：637 - 642
摘 要：The aim of this research was to introduce a new, facile and simple method for synthesis of Dy2O3 nanostructures at room temperature. For the first time,galvanostatic electrodeposition was used to synthesize Dy2O3 particles, and the influence of the current density on the structure and morphology of the product was studied.The samples were characterized by X-ray diffraction（XRD）, transmission electron microscopy（TEM） and Brunauer–Emmett–Teller（BET）. The results show that the current density has little effect on the chemical composition but great effect on the structure and morphology of the samples. The average size of the particles decreases as the applied current density increases. The grain size of asprepared samples decreases from 500 to 70 nm when the current density increases from 0.5 to 6.0 mA·cm-2. To obtain oxide product, the as-prepared samples were heattreated at 1,000 °C. The results show that the heat-treated samples have smaller particles. The XRD results show that the similar patterns are observed in the samples synthesized at different current densities, and the only difference from the JCPDS card is the ratio of peak intensities. With the increase in the current density, a decrease in the current efficiency is observed.
Taher Yousefi，Meisam Torab-Mostaedi，Abolfazl Aghaei，Hossein Ghasemi-Mobtaker
摘 要：The aim of this research was to introduce a new, facile and simple method for synthesis of Dy2O3 nanostructures at room temperature. For the first time,galvanostatic electrodeposition was used to synthesize Dy2O3 particles, and the influence of the current density on the structure and morphology of the product was studied.The samples were characterized by X-ray diffraction（XRD）, transmission electron microscopy（TEM） and Brunauer–Emmett–Teller（BET）. The results show that the current density has little effect on the chemical composition but great effect on the structure and morphology of the samples. The average size of the particles decreases as the applied current density increases. The grain size of asprepared samples decreases from 500 to 70 nm when the current density increases from 0.5 to 6.0 mA·cm-2. To obtain oxide product, the as-prepared samples were heattreated at 1,000 °C. The results show that the heat-treated samples have smaller particles. The XRD results show that the similar patterns are observed in the samples synthesized at different current densities, and the only difference from the JCPDS card is the ratio of peak intensities. With the increase in the current density, a decrease in the current efficiency is observed.
关键词：