Magnetic properties and magnetization behavior of SmCo-based magnets with TbCu7-type structure
来源期刊：Journal of Rare Earths2013年第3期
论文作者：泮敏翔 张朋越 葛洪良 吴琼 俞能君
文章页码：262 - 266
摘 要：The nanocrystalline magnets with nominal compositions of Sm1-xLuxCo6.8Zr0.2（x=0,0.2,0.4,0.6）were prepared directly by the intensive milling.The effects of Lu content on the phase structure,the magnetic properties,and magnetization behaviors were also investigated.The XRD patterns of the as-milled samples showed a single SmCo7 phase with TbCu7 structure.Lu addition was proved to result in relevant improvements in the microstructure and magnetic properties,especially in the maximum energy product（BH）max.It was shown that a higher maximum energy product and coercivity of about 17.47 kJ/m3 and 473.45 kA/m were obtained in the sample with x=0.2.From the analysis of the magnetization reversal behavior,it was found that a stronger intergrain exchange coupling interaction was observed in the samples with Lu-doping.From the studies of the coercivity mechanism,it was shown that nucleation model was the dominant magnetization reversal process at the elevated temperature.
泮敏翔，张朋越，葛洪良，吴琼，俞能君
Magnetism Key Laboratory of Zhejiang Province,China Jiliang University
摘 要：The nanocrystalline magnets with nominal compositions of Sm1-xLuxCo6.8Zr0.2（x=0,0.2,0.4,0.6）were prepared directly by the intensive milling.The effects of Lu content on the phase structure,the magnetic properties,and magnetization behaviors were also investigated.The XRD patterns of the as-milled samples showed a single SmCo7 phase with TbCu7 structure.Lu addition was proved to result in relevant improvements in the microstructure and magnetic properties,especially in the maximum energy product（BH）max.It was shown that a higher maximum energy product and coercivity of about 17.47 kJ/m3 and 473.45 kA/m were obtained in the sample with x=0.2.From the analysis of the magnetization reversal behavior,it was found that a stronger intergrain exchange coupling interaction was observed in the samples with Lu-doping.From the studies of the coercivity mechanism,it was shown that nucleation model was the dominant magnetization reversal process at the elevated temperature.
关键词：