Infl uence of Specimen Size on Compression Behavior of Cement Paste and Mortar under High Strain Rates
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2016年第2期
论文作者：陈徐东 CHEN Chen QIAN Pingping XU Lingyu
文章页码：300 - 306
摘 要：Static and dynamic compression tests were carried out on mortar and paste specimens of three sizes（Ф68 mm×32 mm,Ф59 mm×29.5 mm and Ф32 mm×16 mm）to study the influence of specimen size on the compression behavior of cement-based materials under high strain rates.The static tests were applied using a universalservo-hydraulic system,and the dynamic tests were applied by a spilt Hopkinson pressure bar（SHPB）system.The experimentalresults show that for mortar and paste specimens,the dynamic compressive strength is greater than the quasi-static one,and the dynamic compressive strength for specimens of large size is lower than those of smallsize.However,the dynamic increase factors（DIF）has an opposite trend.Obviously,both strain rate and size effect exist in mortar and paste.The test results were then analyzed using Weibull,Carpinteriand Ba?ant’s size effect laws.A good agreement between these three laws and the test results was reached on the compressive strength.However,for the experimentalresults of paste and cement mortar,the size effect is not evident for the peak strain and elastic modulus of paste and cement mortar.
陈徐东，CHEN Chen，QIAN Pingping，XU Lingyu
College of Civil and Transportation Engineering,Hohai University
摘 要：Static and dynamic compression tests were carried out on mortar and paste specimens of three sizes（Ф68 mm×32 mm,Ф59 mm×29.5 mm and Ф32 mm×16 mm）to study the influence of specimen size on the compression behavior of cement-based materials under high strain rates.The static tests were applied using a universalservo-hydraulic system,and the dynamic tests were applied by a spilt Hopkinson pressure bar（SHPB）system.The experimentalresults show that for mortar and paste specimens,the dynamic compressive strength is greater than the quasi-static one,and the dynamic compressive strength for specimens of large size is lower than those of smallsize.However,the dynamic increase factors（DIF）has an opposite trend.Obviously,both strain rate and size effect exist in mortar and paste.The test results were then analyzed using Weibull,Carpinteriand Ba?ant’s size effect laws.A good agreement between these three laws and the test results was reached on the compressive strength.However,for the experimentalresults of paste and cement mortar,the size effect is not evident for the peak strain and elastic modulus of paste and cement mortar.
关键词：