Preparation and Structural Analysis of Montmorillonite Composites
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2009年第6期
论文作者：付桂珍
文章页码：931 - 934
摘 要：Calcium montmorillonite from Liao-ning was organically intercalated by using cety1 trimethy1 ammonium bromide after it was treated with sodium carbonate. The optimal dosage of intercalating agent was tested. The organically intercalated montmorillonite composites were characterized by the methods of XRD, FTIR and DTA/TG. The results show that the intercalating effect of the organically intercalated montmorillonite composite is the best when the amount of intercalating agent reached 120% cation exchange capacity （CEC）
付桂珍
School of Resources and Environmental Engineering,Wuhan University of Technology
摘 要：Calcium montmorillonite from Liao-ning was organically intercalated by using cety1 trimethy1 ammonium bromide after it was treated with sodium carbonate. The optimal dosage of intercalating agent was tested. The organically intercalated montmorillonite composites were characterized by the methods of XRD, FTIR and DTA/TG. The results show that the intercalating effect of the organically intercalated montmorillonite composite is the best when the amount of intercalating agent reached 120% cation exchange capacity （CEC）
关键词：