Synthesis and photoluminescence properties of octahedral K2(Ge,Si)F6:Mn4+ red phosphor for white LED

来源期刊:JOURNAL OF RARE EARTHS2016年第12期

论文作者:金玉明 刘荣辉 陈观通 刘元红 马小乐 邵冷冷 王磊

文章页码:1173 - 1178

摘    要:A novel red-emitting K2(Ge,Si)F6:Mn4+ phosphor with uniform morphology was synthesized by co-precipitation method. The pure K2GeF6 phase with P63 mc space group other than P3m1 space group was affirmed just by incorporation of Si in K2GeF6 at room temperature according to XRD characterization. SEM images showed lamellar and octahedron grain morphology for K2GeF6:Mn4+ and K2(Ge,Si)F6:Mn4+ phosphors, respectively. It was also found that the photoluminescence excitation(PLE) and photoluminescence(PL) showed slight displacement in K2GeF6:Mn4+ and K2(Ge,Si)F6:Mn4+ system. And the zero-phonon line(ZPL) of the PL spectrum of K2GeF6:Mn4+ with Si showed a strong peak. Meanwhile crystalline field surrounding Mn4+ changes could affect the decay time in this fluoride system. The color gamut of the LED devices based on K2(Ge,Si)F6:Mn4+ and K2GeF6:Mn4+ reached up to 94.58% NTSC(National Television Standards Committee) and 94.386% NTSC, respectively, that was much higher than that based on nitride red phosphors. All these original characteristics in K2(Ge,Si)F6:Mn4+ phosphor are desirable for potential applications as a red phosphor for improving lighting and display quality of conventional white LEDs.

详情信息展示

Synthesis and photoluminescence properties of octahedral K2(Ge,Si)F6:Mn4+ red phosphor for white LED

金玉明,刘荣辉,陈观通,刘元红,马小乐,邵冷冷,王磊

National Engineering Research Center for Rare Earth Materials,General Research Institute for Nonferrous Metals,and Grirem Advanced Materials Co.,Ltd.

摘 要:A novel red-emitting K2(Ge,Si)F6:Mn4+ phosphor with uniform morphology was synthesized by co-precipitation method. The pure K2GeF6 phase with P63 mc space group other than P3m1 space group was affirmed just by incorporation of Si in K2GeF6 at room temperature according to XRD characterization. SEM images showed lamellar and octahedron grain morphology for K2GeF6:Mn4+ and K2(Ge,Si)F6:Mn4+ phosphors, respectively. It was also found that the photoluminescence excitation(PLE) and photoluminescence(PL) showed slight displacement in K2GeF6:Mn4+ and K2(Ge,Si)F6:Mn4+ system. And the zero-phonon line(ZPL) of the PL spectrum of K2GeF6:Mn4+ with Si showed a strong peak. Meanwhile crystalline field surrounding Mn4+ changes could affect the decay time in this fluoride system. The color gamut of the LED devices based on K2(Ge,Si)F6:Mn4+ and K2GeF6:Mn4+ reached up to 94.58% NTSC(National Television Standards Committee) and 94.386% NTSC, respectively, that was much higher than that based on nitride red phosphors. All these original characteristics in K2(Ge,Si)F6:Mn4+ phosphor are desirable for potential applications as a red phosphor for improving lighting and display quality of conventional white LEDs.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号