Effect of rare earths surface treatment on tribological properties of carbon fibers reinforced PTFE composite under oil-lubricated condition
来源期刊：Journal of Rare Earths2008年第4期
论文作者：上官倩芡 程先华
文章页码：584 - 589
摘 要：The effect of rare earths （RE） surface treatment of carbon fibers （CF） on tribological properties of CF reinforced polytetrafluoroethylene （PTFE） composites under oil-lubricated condition was investigated. Experimental results revealed that RE treated CF reinforced PTFE （CF/PTFE） composite had the lowest friction coefficient and wear under various applied loads and sliding speeds compared with untreated and air-oxidated composites. X-ray photoelectron spectroscopy （XPS） study of carbon fiber surface showed that, after RE treatment, oxygen concentration increased obviously, and the amount of oxygen-containing groups on CF surfaces were largely increased. The increase in the amount of oxygen-containing groups enhanced interfacial adhesion between CF and PTFE matrix. With strong interfacial adhesion of the composite, stress could be effectively transmitted to carbon fibers; carbon fibers were strongly bonded with PTFE matrix, and large scale rubbing-off of PTFE be prevented, therefore, tribological properties of the composite was improved.
上官倩芡，程先华
摘 要：The effect of rare earths （RE） surface treatment of carbon fibers （CF） on tribological properties of CF reinforced polytetrafluoroethylene （PTFE） composites under oil-lubricated condition was investigated. Experimental results revealed that RE treated CF reinforced PTFE （CF/PTFE） composite had the lowest friction coefficient and wear under various applied loads and sliding speeds compared with untreated and air-oxidated composites. X-ray photoelectron spectroscopy （XPS） study of carbon fiber surface showed that, after RE treatment, oxygen concentration increased obviously, and the amount of oxygen-containing groups on CF surfaces were largely increased. The increase in the amount of oxygen-containing groups enhanced interfacial adhesion between CF and PTFE matrix. With strong interfacial adhesion of the composite, stress could be effectively transmitted to carbon fibers; carbon fibers were strongly bonded with PTFE matrix, and large scale rubbing-off of PTFE be prevented, therefore, tribological properties of the composite was improved.
关键词：