Effect of thermal exposure on the microstructure and creep properties of a fourth-generation Ni-based single crystal superalloy
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2021年第10期
论文作者：Yeshun Huang Xinguang Wang Chuanyong Cui Zihao Tan Jinguo Li Yanhong Yang Jinlai Liu Yizhou Zhou Xiaofeng Sun
文章页码：180 - 187
摘 要：The effect of thermal exposure on microstructure and creep properties of a fourth-generation nickelbased single crystal superalloy was investigated.The thermal exposure of samples after the full heat treatment was carried out at 1000℃,1100℃ and 1140℃ for 100 h and 200 h.The γ’ coarsening,γ’ rafting and γ channel widening were observed in samples after thermal exposure.When the thermal exposure time was constant,the morphology of γ’ phase in the alloy evolved significantly with increasing aging temperature.The interracial dislocation networks in aged samples after creep ruptured gradually became irregular and sparse with the increase of exposure temperature.When the higher exposure temperature was used,enla rgement of the defect pores was observed in samples,the microcracks were more likely to initiate and propagate at the corner of these pores.After aging at 1000℃ for 100 h,the creep life at 1140℃/137 MPa was slightly longer than that of heat-treated sample,which could be attributed to the slightly coarsened γ’ phase,homogenization of refractor elements.In contrast,the creep life of sample exposed at 1140℃ for 100 h was greatly decreased.The decrease of creep life was dominated by the rafting of γ’phase,the irregular interfacial dislocation networks as well as the enlargement of homogenization pores.
Yeshun Huang1,2，Xinguang Wang1，Chuanyong Cui1，Zihao Tan1，Jinguo Li1，Yanhong Yang1，Jinlai Liu1，Yizhou Zhou1，Xiaofeng Sun1
1. Institute of Metal Research, Chinese Academy of Sciences2. School of Materials Science and Engineering, University of Science and Technology of China
摘 要：The effect of thermal exposure on microstructure and creep properties of a fourth-generation nickelbased single crystal superalloy was investigated.The thermal exposure of samples after the full heat treatment was carried out at 1000℃,1100℃ and 1140℃ for 100 h and 200 h.The γ’ coarsening,γ’ rafting and γ channel widening were observed in samples after thermal exposure.When the thermal exposure time was constant,the morphology of γ’ phase in the alloy evolved significantly with increasing aging temperature.The interracial dislocation networks in aged samples after creep ruptured gradually became irregular and sparse with the increase of exposure temperature.When the higher exposure temperature was used,enla rgement of the defect pores was observed in samples,the microcracks were more likely to initiate and propagate at the corner of these pores.After aging at 1000℃ for 100 h,the creep life at 1140℃/137 MPa was slightly longer than that of heat-treated sample,which could be attributed to the slightly coarsened γ’ phase,homogenization of refractor elements.In contrast,the creep life of sample exposed at 1140℃ for 100 h was greatly decreased.The decrease of creep life was dominated by the rafting of γ’phase,the irregular interfacial dislocation networks as well as the enlargement of homogenization pores.