Flexural Strength and Weibull Analysis of Bulk Metallic Glasses
来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2016年第2期
论文作者:Jijun Zhang Diana Estévez Yuan-Yun Zhao Lishan Huo Chuntao Chang Xinmin Wang Run-Wei Li
文章页码:129 - 133
摘 要:The flexural strength reliability of bulk metallic glasses(BMGs) plates is analyzed using Weibull statistics.The Weibull modulus(m) and characteristic strength(σ0) of the Zr48Cu45Al7 BMG are 34 and 2630 MPa,respectively,which are much higher than the values of fine ceramics(m<30,σ0< 1600 MPa).In particular,the m values obtained by flexural strength and compressive strength statistics of the Mg61Cu28Gd11BMG are 5 and 33,respectively,indicating that the m values of BMGs are test method dependent,and only the m values obtained by flexural strength statistics can be used to make a convincible comparison with those of ceramics.
Jijun Zhang1,2,Diana Estévez1,2,Yuan-Yun Zhao1,2,Lishan Huo1,2,Chuntao Chang1,2,Xinmin Wang1,2,Run-Wei Li1,2
1. Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences2. Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences
摘 要:The flexural strength reliability of bulk metallic glasses(BMGs) plates is analyzed using Weibull statistics.The Weibull modulus(m) and characteristic strength(σ0) of the Zr48Cu45Al7 BMG are 34 and 2630 MPa,respectively,which are much higher than the values of fine ceramics(m<30,σ0< 1600 MPa).In particular,the m values obtained by flexural strength and compressive strength statistics of the Mg61Cu28Gd11BMG are 5 and 33,respectively,indicating that the m values of BMGs are test method dependent,and only the m values obtained by flexural strength statistics can be used to make a convincible comparison with those of ceramics.
关键词: