Sol-Gel Preparation of Zn2 SiO4 :Mn Phosphor Layers on Silica Spheres and Their Luminescent Properties
来源期刊：JOURNAL OF RARE EARTHS2004年增刊第1期
论文作者：Lin Cuikun Yu Min Lin Jun Kong Deyan
Key words：sol-gel; core-shell phosphor; zinc orthosilicate; Mn2 +; silica; rare earths;
Abstract: The synthesis and luminescence properties of Zn2 SiO4: Mn phosphor layers on spherical silica spheres, i.e.,a kind of core-shell complex phosphor, Zn2SiO4: Mn@ SiO2 were described.Firstly, monodisperse silica spheres were obtained via the Stober method by the hydrolysis of tetraethoxysilane(TEOS) Si ( OC2H5 ) 4 under base condition ( using NH4 OH as the catalyst).Secondly, the silica spheres were coated with a Zn2 SiO4: Mn phosphor layer by a Pechini solgel process.X-ray diffraction ( XRD), scanning electron microscope ( SEM), energy-dispersive X-ray spectrum ( EDS )and photoluminescence (PL) were employed to characterize the resulting complex phosphor.The results confirm that1000 ℃ annealed sample consists of crystalline Zn2SiO4: Mn shells and amorphous SiO2 cores.The phosphor show the green emission of Mn2+ at 521 nm corresponding 4T1 (4G) - 6 A1 (6S) transition, and the possible luminescence mechanism is proposed.
Lin Cuikun1，Yu Min1，Lin Jun1，Kong Deyan1
(1.Key laboratory of Rare Earth Chemistry and Physics, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China)
Abstract:The synthesis and luminescence properties of Zn2 SiO4: Mn phosphor layers on spherical silica spheres, i.e.,a kind of core-shell complex phosphor, Zn2SiO4: Mn@ SiO2 were described.Firstly, monodisperse silica spheres were obtained via the Stober method by the hydrolysis of tetraethoxysilane(TEOS) Si ( OC2H5 ) 4 under base condition ( using NH4 OH as the catalyst).Secondly, the silica spheres were coated with a Zn2 SiO4: Mn phosphor layer by a Pechini solgel process.X-ray diffraction ( XRD), scanning electron microscope ( SEM), energy-dispersive X-ray spectrum ( EDS )and photoluminescence (PL) were employed to characterize the resulting complex phosphor.The results confirm that1000 ℃ annealed sample consists of crystalline Zn2SiO4: Mn shells and amorphous SiO2 cores.The phosphor show the green emission of Mn2+ at 521 nm corresponding 4T1 (4G) - 6 A1 (6S) transition, and the possible luminescence mechanism is proposed.
Key words:sol-gel; core-shell phosphor; zinc orthosilicate; Mn2 +; silica; rare earths;