Preparation and photoluminescence enhancement of Li+ and Eu3+ co-doped YPO4 hollow microspheres
来源期刊:JOURNAL OF RARE EARTHS2013年第5期
论文作者:张立新 酒红芳 付跃华 孙益新 王瑗钟
文章页码:449 - 455
摘 要:Li+ and Eu3+ co-doped YPO4 hollow microspheres were successfully synthesized by a sacrificial template method using polystyrene (PS) as template. Techniques of X-ray diffraction (XRD), scanning electron microscopy (SEM), as well as transmission electron microscopy (TEM) were employed to characterize the as-synthesized sample. Furthermore, the photoluminescence (PL) characterization of the Li+ and Eu3+ co-doped YPO4 microsphere was carried out and the effects of the doping concentration of Li+ and Eu3+ active center concentration as well as calcination temperature on the PL properties were studied in detail. The results showed that the incorporation of Li+ ions into the YPO4 :Eu3+ lattice could induce a remarkable improvement of the PL intensity. The highest emission intensity was observed with the compound of 5%Li+ and 5%Eu3+ co-doped YPO4 , whose brightness was increased by a factor of more than 2.2 in comparison with that of the YPO4 :5%Eu3+.
张立新1,酒红芳2,付跃华2,孙益新1,王瑗钟1
1. Chemical Engineering and Environment Institute,North University of China2. College of Science,North University of China
摘 要:Li+ and Eu3+ co-doped YPO4 hollow microspheres were successfully synthesized by a sacrificial template method using polystyrene (PS) as template. Techniques of X-ray diffraction (XRD), scanning electron microscopy (SEM), as well as transmission electron microscopy (TEM) were employed to characterize the as-synthesized sample. Furthermore, the photoluminescence (PL) characterization of the Li+ and Eu3+ co-doped YPO4 microsphere was carried out and the effects of the doping concentration of Li+ and Eu3+ active center concentration as well as calcination temperature on the PL properties were studied in detail. The results showed that the incorporation of Li+ ions into the YPO4 :Eu3+ lattice could induce a remarkable improvement of the PL intensity. The highest emission intensity was observed with the compound of 5%Li+ and 5%Eu3+ co-doped YPO4 , whose brightness was increased by a factor of more than 2.2 in comparison with that of the YPO4 :5%Eu3+.
关键词: