Synthesis and characterization of Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 by wet chemical route
来源期刊：Rare Metals2009年第2期
论文作者：WU Xianming,LI Runxiu,CHEN Shang,and HE Zeqiang College of Chemistry and Chemical Engineering,Jishou University,Jishou ,China
文章页码：122 - 126
摘 要：Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 was prepared by wet chemical route. The phase,surface morphology,and electrochemical properties of the prepared powders were characterized by X-ray diffraction,scanning electron micrograph,and galvanostatic charge-discharge experiments. Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 has similar X-ray diffraction patterns as LiMn2O4. The corner and border of Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 particles are not as clear as the uncoated one. The two powders show similar values of lithiumion diffusion coefficient. When cycled at room temperature and 55°C for 40 times at the charge-discharge rate of 0.2C,Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 shows the capacity retentions of 98.2% and 93.9%,respectively,which are considerably higher than the values of 85.4% and 79.1% for the uncoated one. Both the capacity retention differences between Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 and LiMn2O4 cycling at room temperature and 55°C become larger with the increase of charge-discharge rate. When the charge-discharge rate reaches 2C,the capacity retention of LATP-coated LiMn2O4 becomes 8.4% higher than the uncoated LiMn2O4 for room temperature cycling,and it becomes 11.1% higher than the latter when cycled at 55°C.
摘要：Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 was prepared by wet chemical route. The phase,surface morphology,and electrochemical properties of the prepared powders were characterized by X-ray diffraction,scanning electron micrograph,and galvanostatic charge-discharge experiments. Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 has similar X-ray diffraction patterns as LiMn2O4. The corner and border of Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 particles are not as clear as the uncoated one. The two powders show similar values of lithiumion diffusion coefficient. When cycled at room temperature and 55°C for 40 times at the charge-discharge rate of 0.2C,Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 shows the capacity retentions of 98.2% and 93.9%,respectively,which are considerably higher than the values of 85.4% and 79.1% for the uncoated one. Both the capacity retention differences between Li1.3Al0.3Ti1.7（PO4）3-coated LiMn2O4 and LiMn2O4 cycling at room temperature and 55°C become larger with the increase of charge-discharge rate. When the charge-discharge rate reaches 2C,the capacity retention of LATP-coated LiMn2O4 becomes 8.4% higher than the uncoated LiMn2O4 for room temperature cycling,and it becomes 11.1% higher than the latter when cycled at 55°C.
关键词：