简介概要

Magnetic properties of melt-spun MM-Fe-B ribbons with different wheel speeds and mischmetal contents

来源期刊：Rare Metals2017年第12期

论文作者：Xue-Feng Zhang Wen-Kai Zhang Yong-Feng Li Yan-Li Liu Zhu-Bai Li Qiang Ma Meng-Fei Shi Fei Liu

文章页码：992 - 996

摘要：In this study, the effect of wheel speed and mischmetal（MM） content on the magnetic properties of MMFeB ribbons was investigated. The samples were prepared via direct solidification technique. The nominal composition of the alloy ingots is MM_xFe_92-xB₈ with x varying from 9 to 15 in steps of 2. Experimental results show the overall magnetic properties of the ribbons.Analysis of the results shows that the magnetic properties first improve and then degrade with the wheel speed and MM content increasing. Increase in MM content leads to better formation of crystal texture in the ribbons, indicating that the a-Fe phase might undermine the formation of crystal texture. Magnetic properties results show that the coercivity of the ribbons rises with an appropriate increase in both MM content and wheel speed during melt-spun process. The strongest magnetic properties of the ribbons(remanence of M_r = 0.72 T, intrinsic coercivity of H_cj = 352.58 kA·m^-1, and maximum energy product of（BH）_max=72.14 kJ·m^-3) are obtained for compositions where x = 13 and a wheel speed of v = 20 m·s^-1.

稀有金属(英文版) 2017,36(12),992-996

Magnetic properties of melt-spun MM-Fe-B ribbons with different wheel speeds and mischmetal contents

Xue-Feng Zhang Wen-Kai Zhang Yong-Feng Li Yan-Li Liu Zhu-Bai Li Qiang Ma Meng-Fei Shi Fei Liu

Key Laboratory of Integrated Exploitation of Bayan Obo Multi-Metal Resources, Inner Mongolia University of Science and Technology

Schools of Mathematics, Physics and Biological Engineering Inner Mongolia University of Science and Technology

收稿日期：17 March 2015

基金：financially supported by the National Natural Science Foundation of China (Nos. 51461033, 51571126, 51541105, and 11547032);the Inner Mongolia Innovative Research Team (No. 3400102);the Inner Mongolia Science Foundation (No. 2013MS0110);the Provincial Major Science and Technology Project of Inner Mongolia (No. 2009J1006);the Baotou Major Research Project Special for Rare Earth (No. 2012R1006);the Inner Mongolia University of Science and Technology Innovation Fund;

Magnetic properties of melt-spun MM-Fe-B ribbons with different wheel speeds and mischmetal contents

Xue-Feng Zhang Wen-Kai Zhang Yong-Feng Li Yan-Li Liu Zhu-Bai Li Qiang Ma Meng-Fei Shi Fei Liu

Key Laboratory of Integrated Exploitation of Bayan Obo Multi-Metal Resources, Inner Mongolia University of Science and Technology

Schools of Mathematics, Physics and Biological Engineering Inner Mongolia University of Science and Technology

Abstract：

In this study, the effect of wheel speed and mischmetal(MM) content on the magnetic properties of MMFeB ribbons was investigated. The samples were prepared via direct solidification technique. The nominal composition of the alloy ingots is MM_xFe_92-xB₈ with x varying from 9 to 15 in steps of 2. Experimental results show the overall magnetic properties of the ribbons.Analysis of the results shows that the magnetic properties first improve and then degrade with the wheel speed and MM content increasing. Increase in MM content leads to better formation of crystal texture in the ribbons, indicating that the a-Fe phase might undermine the formation of crystal texture. Magnetic properties results show that the coercivity of the ribbons rises with an appropriate increase in both MM content and wheel speed during melt-spun process. The strongest magnetic properties of the ribbons(remanence of M_r = 0.72 T, intrinsic coercivity of H_cj = 352.58 kA·m^-1, and maximum energy product of(BH)_max=72.14 kJ·m^-3) are obtained for compositions where x = 13 and a wheel speed of v = 20 m·s^-1.

Keyword：

Mischmetal; MMFeB; Magnetic properties; Melt spun;

Author： Yong-Feng Li e-mail: wuleng@126.com;

Received： 17 March 2015

1 Introduction

Since its discovery in 1983 [ 1] ,sintered NdFeB permanent magnets have become the fastest growing and most widely used rare earth permanent magnetic material because of its excellent comprehensive magnetic performance.This performance continues to improve through advancements in preparative techniques and composition optimization [ 2, 3, 4, 5] .At present,the need of sintered rare earth permanent magnets material has been increasing in the market [ 6] .In recent years,raw materials such as the metals Nd and Pr used in preparing NdFeB materials have become scarcer,which results in a sharp rise in the price of materials for sintered NdFeB permanent magnets and creates enormous challenges for the sintered NdFeB industry.Because of the cost pressure of PrNd and Dy metals,the issue on substitution of PrNd by mischmetal(MM) alloys attracted renewed attention [ 7] and another issue is that both Nd and Pr are extracted from mixed accretive rare earth mines,which are typically also rich in La and Ce [ 8, 9] ,and the cost of separating the rare earths is very high.On the other hand,La,Ce,Pr,and Nd are all4f atom elements with a hexagonal close-packed (hcp)structure,so they can form chemical compounds of MM₂Fe₁₄B with MM,Fe,and B [ 10] .Furthermore,La and Ce are effective in refining the grain size of these ribbons [ 11] ,and MMFeB is possible to be a potential nanocomposite magnetic material [ 12] .Therefore,it is possible to adjust the components used to create rare earth magnets so that they can better meet the available resource conditions in order to reduce costs and optimize resources [ 13] .In previous work,the common mixed rare earth metal MM which consists of large amounts of La and Ce and a small amount of Pr and Nd was used to prepare MM-Fe-B melt-spun ribbons.

In this paper,it is focused on how MM content (x) and quenching wheel speed (v) influence the microstructure and magnetic properties of the material,with the purpose of developing better magnetic properties in MMFeB magnets.

2 Experimental

In this experiment,MM is a very common mischmetal from Bay an Obo mine in Baotou,China,and it consists of La28.63 wt%,Ce 50.13 wt%,Pr 4.81 wt%,Nd 16.38 wt%,and a few other impurities.Alloy ingots with a nominal composition of MM_xFe_92-xB₈ (x=9,11,13,15) were prepared using a high-frequency melting furnace with MM,Fe,and FeB components under high-purity Ar atmosphere.The ingots were melted three times and thermally treated for120 min to ensure homogeneity of the ingots.The arc-melt ingots were broken into small pieces and crushed into quartz tubes,and then melt-spun onto a copper wheel in argon atmosphere under different wheel speeds of 10,15,20,25,30,40,and 50 m·s^-1.The phases and grain sizes of the samples were characterized using X-ray diffraction (XRD,D8 ADVANCE) with Cu Kαradiation.The magnetic hysteresis loops of the ribbons were measured using a vibrating sample magnetometer (VSM,Quantum Design VersaLab)with an applied field up to 3 T.The microstructure of the MM₁₃Fe₇₉B₈ alloy ingots was characterized by scanning electron microscope (SEM,QUANTA 400) equipped with energy-dispersive spectroscopy (EDS).

3 Results and discussion

3.1 Structure and magnetic properties of melt-spun ribbons at different wheel speeds

Figure 1 shows the XRD patterns of melt-spun ribbons with different compositions at wheel speeds of 10,15,20,25,30,40,and 50 m·s^-1.As shown,the diffraction peak of theα-Fe phase disappears and the peak intensity of MM₂Fe₁₄B gradually strengthens as the MM content increases,which indicates that the number of MM₂Fe₁₄B phases in the sample increases as MM content increases.In addition,it is obvious that the diffraction pattern of the ribbons gradually widens with wheel speed increasing [ 14] ,suggesting that the average grain size decreases.

Table 1 shows the average grain size of the melt-spun ribbons with different compositions at wheel speeds of 10,15,20,25,30,40,and 50 m·s^-1.Zhao et al. [ 15] reported that the relationship between remanence enhancement and grain size can be written as:

where M_r,M_s,⊿₀,and L are the remanence,saturation magnetization,exchange length,and average grain size,respectively.At x=13 and v=20 m·s^-1,the ribbons have properties of M_s=1.23 T,M_r=0.72 T,and⊿₀=4/π.The result of M_r/M_s is 0.585 and 0.5+1.8⊿₀/L is 0.548,which are in good agreement with the model of remanence enhancement.

Fig.1 XRD patterns of MM_xFe_92-xB₈ melt-spun ribbons under different wheel speeds:a x=9,b x=11,and c x=13

下载原图

Table 1 Average grain size of MM_xFe_92-xB₈ (x=9,11,13,15) melt-spun ribbons at wheel speeds of 10,20,25,30,40,and 50 m·s^-1 (nm)

Fig.2 Hysteresis loop of MM₁₃Fe₇₉B₈ melt-spun ribbons produced under different wheel speeds

Figure 2 presents the magnetic hysteresis loops of the MM₁₃Fe₇₉B₈ melted ribbons melt spun at wheel speeds of10,15,20,25,30,40,and 50 m·s^-1.Note that the squareness of the hysteresis loop is poor at very low and very high wheel speeds,while the demagnetization curves at wheel speeds of 15 and 20 m·s^-1 are very smooth.Figure 3 shows the variation in maximum M_r,coercivity(H_cj),and maximum energy product ((BH)_max) values as a function of wheel speed for the MM₁₃Fe₇₉B₈ melt-spun ribbons.All of the ribbons’magnetic properties (M_r,H_cj,and first increase as the wheel speed increases up to 20 m·s^-1 and then decrease.The best magnetic properties are obtained at a wheel speed of 20 m·s^-1,achieving an M_r value of 0.72 T,an H_cj value of 352.58 kA·m^-1,and a (BH)_max value of 72.14 kJ·m^-3.

Fig.3 Variation in maximum values for M_r,H_cj,and (BH)_max of MM₁₃Fe₇₉B₈ melt-spun ribbons as a function of wheel speed

Fig.4 SEM-BSE image of MM₁₃Fe₇₉B₈ alloy ingot and elemental EDS line scan maps across matrix phase and rare earth phase regions:a SEM-BSE image,b Pr,c Nd,d Fe,e La,and f Ce

3.2 Rare earth and Fe distribution in melt-spun ribbons

From the backscattered electron (BSE) map of the MM₁₃Fe₇₉B₈ ingot in Fig.4,the compositional variation that occurs across the region in the EDS intensity profiles can be clearly seen.The scanned region can be pided into a Re-rich phase in which Fe content is low,and a matrix phase in which Fe content is high.This suggests that Ce has a stronger affinity with Nd,while La has a stronger affinity with Pr.Thus,La,Pr,Fe,and B preferentially form(PrLa)₂Fe₁₄B as a metallic phase.Furthermore,when Pr,Nd,and La contents are lower,Ce content is spiked,indicating that the excess Ce,Fe,and B form Ce₂Fe₁₄B phase in these ribbons instead.

3.3 Magnetic properties of melt-spun ribbons with different MM contents

The magnetic properties of MM_xFe_92-xB₈ (x=9,11,13,15) melt-spun ribbons prepared at wheel speeds of 10,15,20,25,30,40,and 50 m·s^-1 were measured by VSM,with the results shown in Table 2.The data in Table 2 show that the magnetic properties of the ribbons all first increase as the MM content increases at wheel speeds of 10,15,20,25,30,40,and 50 m·s^-1.This result indicates that increasing the MM content leads to the production of a harder magnetic phase MM₂Fe₁₄B alloy with a corresponding decrease in theα-Fe phase,resulting in the enhancement of the remanence and coercivity of the ribbons.Therefore,the remanence,coercivity,and maximum energy product all correspondingly increase.

Furthermore,it can be seen that all of the magnetic properties (M_r,H_cj,and (BH)_max) also first increase as the wheel speed increases for a given composition.In this scenario,the average grain size of the ribbon decreases as the wheel speed increases,and this gradually enhances the coercivity of the ribbon.Therefore,the coercivity and the maximum energy product increase together.However,it is worth noting that the coercivity of the ribbons drops precipitously beyond a wheel speed of 20 m·s^-1.Meanwhile,for the ribbons with the same composition,the relative intensity and the quantity of diffraction peaks for MM₂Fe₁₄B phase decrease with wheel speed increasing,indicating that the amount of MM₂Fe₁₄B phase decreases and that of amorphous increases with wheel speed increasing [ 16] .

下载原图

Table 2 Magnetic properties of MM_xFe_92-xB₈ (x=9,11,13,15)melt-spun ribbons with different wheel speeds (v) and MM content (x)

4 Conclusion

MMxFe92-xB8 (x=9,11,13,15) magnetic ribbons were prepared by direct solidification,and the effect of MM content and wheel speed on the microstructure and the magnetic properties of the melt-spun ribbons was investigated.X-ray analysis shows that increasing MM content and wheel speed cause theα-Fe phase to disappear and the peak intensity of the MM₂Fe₁₄B phase to gradually strengthen,indicating that increasing MM content leads to a beneficial formation of the MM₂Fe₁₄B phase in the ribbon.VSM results show that M_r,H_cj,and (BH)_max of the optimally processed MM_xFe_92-xB₈ ribbons first increase with the increase in wheel speed,reaching maximum values at v=20 m·s^-1,and then decrease with further increase in wheel speed.The results also show that the magnetic properties of the ribbons first increase with MM content increasing,reaching their maximum values at x=13.Beyond this MM content,however,these properties decrease.In conclusion,it is able to produce melt-spun ribbons with excellent magnetic properties:M_s=1.23 T,M_r=0.72 T,H_cj=352.58 kA·m^-1,and (BH)_max=72.14 kJ·m^-3,using an MM content of x=13 (i.e.,MM₁₃Fe₇₉B₈) and a wheel speed v=20 m·s^-1.

Acknowledgments This work was financially supported by the National Natural Science Foundation of China (Nos.51461033,51571126,51541105,and 11547032),the Inner Mongolia Innovative Research Team (No.3400102),the Inner Mongolia Science Foundation(No.2013MS0110),the Provincial Major Science and Technology Project of Inner Mongolia (No.2009J1006),the Baotou Major Research Project Special for Rare Earth (No.2012R1006),and the Inner Mongolia University of Science and Technology Innovation Fund.