Synthesis of ZSM-5@ Ordered Mesoporous Silica Composites by Dodecylamine Surfactant
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2014年第6期
论文作者：马扩彦 俞海军 FENG Guanglin WANG Changguo 戴亚
文章页码：1124 - 1128
摘 要：The core-shell structures of ZSM-5 coated with mesoporous silica were synthesized by means of dodecylamine（DDA） surfactant. The results show that the mesoporous silica shells are coated on ZSM-5 cores and result in the formation of hierarchical porous structures. The thickness of the coating shell can be controlled by changing the adding amount of TEOS. The core-shell composites with the thickness of 35 nm possess high surface areas（about 528 m2·g-1）, large pores（about 3.5 nm in diameter） on the silica shells. The composite molecular sieves display higher adsorption capacity for benzene（140.2 mg·g-1） and butyraldehyde（213.7 mg·g-1） than that of pristine ZSM-5 for benzene（99.2 mg·g-1） and butyraldehyde（134.7 mg·g-1）. The composite molecular sieves show a wide application foreground for harmful gas adsorbent for environmental protection.
马扩彦1,2，俞海军1,2，FENG Guanglin1,2，WANG Changguo1,2，戴亚1,2
2. Chuanyu Branch of China Tobacco Corporation
摘 要：The core-shell structures of ZSM-5 coated with mesoporous silica were synthesized by means of dodecylamine（DDA） surfactant. The results show that the mesoporous silica shells are coated on ZSM-5 cores and result in the formation of hierarchical porous structures. The thickness of the coating shell can be controlled by changing the adding amount of TEOS. The core-shell composites with the thickness of 35 nm possess high surface areas（about 528 m2·g-1）, large pores（about 3.5 nm in diameter） on the silica shells. The composite molecular sieves display higher adsorption capacity for benzene（140.2 mg·g-1） and butyraldehyde（213.7 mg·g-1） than that of pristine ZSM-5 for benzene（99.2 mg·g-1） and butyraldehyde（134.7 mg·g-1）. The composite molecular sieves show a wide application foreground for harmful gas adsorbent for environmental protection.
关键词：