Photocatalytic Activity of Porous Magnesium Oxychloride Cement Combined with AC/TiO2 Composites
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2017年第3期
论文作者：冯传法 王发洲 LIU Peng SUN Guoxin YANG Lu ZHANG Wenqin SHU Chang
文章页码：591 - 597
摘 要：As a decorative material, magnesium oxychloride cement was used as a photocatalyst supporter to purify the pollutants indoors. Due to excellent adsorption properties of activated carbon（AC）, the photocatalytic composties, TiO2/AC, were prepared and introduced into the porous magnesium oxychloride cement（PMOC） substrate to composite a sort of photocatalytic cementitious material（PCM）. The optimal composite processes were assessed by gas chromatograph, using toluene as the target. By comparing the perspective of toluene purification and thorough decomposition, it can be found that the optimal mass ratio for TiO2/AC composites is 4/25, and the heat treatment to TiO2/AC sample at 350 ℃ can play the optimal synergetic role of adsorbents in photocatalytic process. The synergistic effect of TiO2, AC and magnesium oxychloride cement（MOC） was also evaluated by gas chromatograph. One-take molding process was adopted to introduce the TiO2/AC into PMOC substrate, and its optimal mass fraction was 4 wt%, while the appropriate density of substrate was 0.35 g/cm3. Toluene degradation showed that the prepared PCM can degrade pollutants efficiently. The appropriate treatment process of TiO2/AC, mass of TiO2/AC, substrate density, and stable pore structure should be coordinated to maximize the adsorption-photodegradation performance. The combination of photocatalytic materials, adsorbents, and building materials provided a new idea for the application of photocatalysis.
冯传法1，王发洲1，LIU Peng1,2，SUN Guoxin1，YANG Lu1，ZHANG Wenqin1，SHU Chang1
1. State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology2. School of Chemistry, Chemical Engineering and Life Science,Wuhan University of Technology
摘 要：As a decorative material, magnesium oxychloride cement was used as a photocatalyst supporter to purify the pollutants indoors. Due to excellent adsorption properties of activated carbon（AC）, the photocatalytic composties, TiO2/AC, were prepared and introduced into the porous magnesium oxychloride cement（PMOC） substrate to composite a sort of photocatalytic cementitious material（PCM）. The optimal composite processes were assessed by gas chromatograph, using toluene as the target. By comparing the perspective of toluene purification and thorough decomposition, it can be found that the optimal mass ratio for TiO2/AC composites is 4/25, and the heat treatment to TiO2/AC sample at 350 ℃ can play the optimal synergetic role of adsorbents in photocatalytic process. The synergistic effect of TiO2, AC and magnesium oxychloride cement（MOC） was also evaluated by gas chromatograph. One-take molding process was adopted to introduce the TiO2/AC into PMOC substrate, and its optimal mass fraction was 4 wt%, while the appropriate density of substrate was 0.35 g/cm3. Toluene degradation showed that the prepared PCM can degrade pollutants efficiently. The appropriate treatment process of TiO2/AC, mass of TiO2/AC, substrate density, and stable pore structure should be coordinated to maximize the adsorption-photodegradation performance. The combination of photocatalytic materials, adsorbents, and building materials provided a new idea for the application of photocatalysis.
关键词：