Hydration Kinetics of Phosphorus Slag-cement Paste
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第1期
论文作者：陈霞
文章页码：142 - 146
摘 要：Hydration characteristics of Portland cement paste with phosphorus slag powder incorporated and hydration kinetics was investigated with SEM, X-ray diffraction, DTA-TG and calorimeter Ⅱ80. Results showed that phosphorus slag powder could reduce total amount of hydration products yet had little influence on the type of hydration products. The total amount of heat of hydration was decreased by 49.11% and the final setting was postponed by 2.28 h when phosphorus slag powder substituted 35% Portland cement by mass. The accelerating stage of this composite paste was controlled by catalysis, decreasing stage controlled by both catalysis and diffusion while stabilizing stage by diffusion alone. Hydration resistance and activation energy were reduced and hydration speed was accelerated.
陈霞
School of Civil Engineering, Wuhan UniversityDepartment of Mateials and Structure, Changjiang River Scientific Research lnstitute
摘 要：Hydration characteristics of Portland cement paste with phosphorus slag powder incorporated and hydration kinetics was investigated with SEM, X-ray diffraction, DTA-TG and calorimeter Ⅱ80. Results showed that phosphorus slag powder could reduce total amount of hydration products yet had little influence on the type of hydration products. The total amount of heat of hydration was decreased by 49.11% and the final setting was postponed by 2.28 h when phosphorus slag powder substituted 35% Portland cement by mass. The accelerating stage of this composite paste was controlled by catalysis, decreasing stage controlled by both catalysis and diffusion while stabilizing stage by diffusion alone. Hydration resistance and activation energy were reduced and hydration speed was accelerated.
关键词：