Electrochemical performance of alloys Ho5Fe3Co12 and Ho33.3Co66.7

来源期刊:JOURNAL OF RARE EARTHS2010年第4期

论文作者:赵允红 何维 张永志 曾令民

文章页码:618 - 621

摘    要:Alloys with composition Ho5Fe3Co12 and Ho33.3Co66.7 were prepared and examined by X-ray diffractometer and automatic battery testing instrument. The electrochemical properties of these alloys such as discharge capacity, cycling performance and high rate dischargeability were investigated by battery testing instruments in alkaline electrolyte. A comparison of the electrochemical performance of the Ho5Fe3Co12 and Ho33.3Co66.7 alloys revealed that alloy Ho5Fe3Co12 possessed a better electrochemical performance and had better discharge capacity, cycle stability and high rate dischargeability. The largest discharge capacity of alloy Ho5Fe3Co12 was about 536.7 mAh/g at discharge current densities 450 and 600 mA/g, and that of alloy Ho33.3Co66.7 was 400 mAh/g at discharge current density of 300 mA/g.

详情信息展示

Electrochemical performance of alloys Ho5Fe3Co12 and Ho33.3Co66.7

赵允红,何维,张永志,曾令民

Key Laboratory of Nonferrous Metal Materials and New Processing Technology, College of Materials Science and Engineering, Guangxi University

摘 要:Alloys with composition Ho5Fe3Co12 and Ho33.3Co66.7 were prepared and examined by X-ray diffractometer and automatic battery testing instrument. The electrochemical properties of these alloys such as discharge capacity, cycling performance and high rate dischargeability were investigated by battery testing instruments in alkaline electrolyte. A comparison of the electrochemical performance of the Ho5Fe3Co12 and Ho33.3Co66.7 alloys revealed that alloy Ho5Fe3Co12 possessed a better electrochemical performance and had better discharge capacity, cycle stability and high rate dischargeability. The largest discharge capacity of alloy Ho5Fe3Co12 was about 536.7 mAh/g at discharge current densities 450 and 600 mA/g, and that of alloy Ho33.3Co66.7 was 400 mAh/g at discharge current density of 300 mA/g.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号